1) repassivation temperature(Tr)
再钝化温度
1.
The critical pitting temperature(CPT) and repassivation temperature(Tr) for two kinds of duplex stainless steels(DSS) were investigated in 1 mol/L NaCl solution at an anodic potential of 750 mV (vs SCE) using the cyclic thermammetry method.
采用外加恒定电位下腐蚀电流密度-温度循环扫描技术,研究两种双相不锈钢(2205和2507)在750 mV(vs SCE)外加电压下1 mol/L NaCl溶液中的临界点蚀温度和再钝化温度,用动电位极化曲线的方法对该实验结果进行验证。
2) passivated temperature
钝化温度
1.
Changing passivated temperature and passivated time,PL of the passivated samples shows an obvious change,and the highest ligh.
结果表明 ,随着氧化电流密度增大 ,PS的微晶 Si平均尺寸减小 ,且尺寸大的微晶 Si数量也减少 ,说明制备条件对钝化 PS的发光有影响 ;PS经适当的高温氧化处理后 ,其 PL 谱会发生明显变化 ;选用含有胺基的正丁胺 ,采用射频辉光放电法对 PS进行钝化处理 ,在一定程度上提高了 PS的发射强度伴随发光峰位的较大蓝移 ;其钝化 PS的荧光谱随钝化温度和钝化时间变化 ,说明钝化条件对钝化 PS的发光有直接影响。
3) repassivation
再钝化
1.
Pitting corrosion and the effect of inhibitors on rebar repassivation in alkaline solution with chloride ions were studied by scanning reference electrode technique.
采用扫描微参比电极技术（ＳＲＥＴ）对钢筋在含氯离子的碱性体系中点蚀行为和缓蚀剂对钢筋再钝化性能的影响进行研究。
2.
This kind of variation would make the decay parameter of repassivation kinetics distort.
这种变化将导致再钝化动力学衰减参数的失真。
3.
repassivation properties have been discussed.
提出了导电辊腐蚀失效的原因；探讨了其影响因素，以及材料腐蚀行为与其钝化、再钝化性能的关系。
4) passivation at room temperature
常温钝化
5) LTP Low Temperature Passivation
低温钝化
6) high-temperature passivation
高温钝化