1) polymer network gel
高分子网络凝胶
1.
With TiCl_3 and (NH_4)_2S_2O_8 as original material,TiO_2 was produced with polymer network gel method.
以 TiCl_3为原料、过硫酸铵为引发剂,采用高分子网络凝胶法制备 TiO_2复合粉体,利用 TEM 和 XRD 对纳米粉体表征。
2) polymer network gel method
高分子网络凝胶法
1.
Synthesis of YAG:Er~(3+) nanoparticles by polymer network gel method and photolum inescene spectrum characters
高分子网络凝胶法制备YAG:Er~(3+)纳米晶粉体及其光谱性质
2.
The topic produces composite powders by TiCl_3 and SnCl_4·5H_2O with polymer network gel method.
以TiCl_3和SnCl_4·5H_2O为原料,采用高分子网络凝胶法制备SnO_2/TiO_2复合粉体。
3) Polymer-network gel method
高分子网络凝胶法
1.
Preparation of AB_5 type hydrogen storage alloy with polymer-network gel method;
高分子网络凝胶法制备AB_5型多元贮氢合金
4) polyacrylamide gel method
高分子网络凝胶法
1.
By using polyacrylamide gel method and sintering at high temperature,Li2O-Al2O3-SiO2-ZrO2(LASZ) glass-ceramic powders were prepared.
采用高分子网络凝胶法成功地制备出Li2O-Al2O3-SiO2-ZrO2(LASZ)微晶玻璃粉,探讨了添加不同含量ZrO2对LASZ微晶玻璃的析晶行为和相转变的影响。
2.
Lithium aluminosilicate(LAS)multicomponent glass-ceramic powders were prepared by using polyacrylamide gel method.
以丙烯酰胺、N,N′亚甲基双丙烯酰胺、碳酸锂、硝酸铝和正硅酸乙酯为原料,采用高分子网络凝胶法成功地制备出多组分氧化物Li2OAl2O3SiO2(LAS)微晶玻璃超微粉末,并掺杂了稀土氧化物Y2O3。
3.
Cordierite powder was prepared by the polyacrylamide gel method using silica-sol as starting material .
利用硅溶胶作为合成原料,通过高分子网络凝胶法制备了堇青石粉。
5) the polyacrylamide gel method
高分子网络凝胶法
1.
Nanoscale α-Al2O3 powders were prepared by the polyacrylamide gel method.
用高分子网络凝胶法制备Ａｌ２Ｏ３粉体，通过网络的阻碍作用，阻止Ａｌ２Ｏ３的团聚，获得颗粒大小在 １０ｎｍ左右的α－Ａｌ２Ｏ３粉体，其煅烧温度比通常低 １００℃。
6) polyacrylamide gel
高分子网络凝胶法
1.
Ultrafine powders of Y_3Al_5O_(12)(YAG):Ce~(3+) were prepared by the polyacrylamide gel,and the spectra characterization,TEM and XRD of the powders was studied.
以高分子网络凝胶法制备Y3A l5O12(YAG):Ce3+微粉,同时对所得微粉使用日本RF—5301pc荧光分光光度计测试其发射光谱和激发光谱,了解其光谱特性,并用TEM分析颗粒形貌,x射线进行物相分析。
2.
Compared with coprecipitation process, YAG phase can be got at lower temperature (900℃) by the polyacrylamide gel.
本文以高分子网络凝胶法制备Y3Al6O12（YAG）：Ce3+微粉，并测试其光谱特性。
3.
Nanoscale composites TiO_2/ZnFe_2O_4 were prepared by the polyacrylamide gel method.
用高分子网络凝胶法制备TiO_2/ZnFe_2O_4纳米复合材料,研究了掺杂ZnFe_2O_4对TiO_2平均粒径、晶型及其光催化性能的影响。
补充资料：Sds-聚丙烯酰胺凝胶电泳凝胶电泳
sds-聚丙烯酰胺凝胶电泳（sds-page，sodium dodecyl sulfate-polyacrylamide gel electrohoresis）
在有去污剂十二烷基硫酸钠存在下的聚丙烯酰胺凝胶电泳。sds-page只是按照分子大小分离的，而不是根据分子所带的电荷和大小分离的。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条