1) porous modified-polypropylene
多孔改性聚碳酸亚丙酯
2) modified Poly(propylene carbonate)
改性聚碳酸亚丙酯
3) poly(propylene carbonate)polyols
聚碳酸亚丙酯多元醇
1.
The thermal stability of poly(propylene carbonate)polyols resin in the presence of residual double metallic catalyst was studied.
研究了残余双金属催化剂存在下聚碳酸亚丙酯多元醇的热稳定性,发现添加质量分数为0。
4) poly(propylene carbonate)
聚碳酸亚丙酯
1.
A novel bio-degradable, biocompatible composite was prepared by introducing surface-coated hydroxyapatite particles into poly(propylene carbonate).
将羟基磷灰石(HA)用硅烷偶联剂KH570处理,然后与聚碳酸亚丙酯(PPC)进行共混,制备了一种可生物降解、生物相容性好的PPC/HA复合材料,研究了其在不同混合比例时的力学性能、玻璃化转变温度及其内部结构。
2.
The degradable composite was made by ramie fibre and poly(propylene carbonate) .
采用苎麻纤维和聚碳酸亚丙酯制备了可降解复合材料,讨论了苎麻长度、含量对苎麻/聚碳酸亚丙酯复合材料机械性能的影响,并借助扫描电子显微镜对复合材料的冲击断口形貌进行了观察。
3.
The blends of poly(β-hydroxybutyrate)(PHB) and poly(propylene carbonate)(PPC) were prepared by solvent volatilizing and melt blending respectively.
采用溶剂挥发法和熔融共混法分别制备了聚β-羟基丁酸酯(PHB)和聚碳酸亚丙酯(PPC)的共混物,采用DSC、X-射线衍射、扫描电镜、偏光显微镜等手段系统研究了共混物配比对体系热、力学性能、形貌的影响。
5) poly (propylene carbonate)
聚碳酸亚丙酯
1.
Biodegradability of Poly (propylene carbonate) /Starch Blend in Municipal Solid Waste;
聚碳酸亚丙酯/淀粉在城市垃圾中生物降解性能研究
6) polytrimethylene carbonate
聚碳酸亚丙基酯
补充资料：聚(异亚丙基二亚苯基碳酸酯
CAS：24936-68-3
中文名称：聚[氧代羰氧基-1,4-亚苯基(1-甲亚乙基)-1,4-亚苯基]
双酚A-光气的聚合物
双酚A聚碳酸酯
聚-4,4'-异亚丙基二苯基碳酸酯
2,2-双(4-羟苯基)丙烷聚碳酸酯
聚(异亚丙基二亚苯基碳酸酯
聚碳酸酯树脂
英文名称：Poly[oxycarbonyloxy-1,4-phenylene(1-methylethylidene)-1,4-phenylene]
Bisphenol A-phosgene polymer
Bisphenol A polycarbonate
Poly-4,4'-isopropylidenediphenyl carbonate)
2,2-bis(4-Hydroxyphenyl)propane polycarbonate
中文名称：聚[氧代羰氧基-1,4-亚苯基(1-甲亚乙基)-1,4-亚苯基]
双酚A-光气的聚合物
双酚A聚碳酸酯
聚-4,4'-异亚丙基二苯基碳酸酯
2,2-双(4-羟苯基)丙烷聚碳酸酯
聚(异亚丙基二亚苯基碳酸酯
聚碳酸酯树脂
英文名称：Poly[oxycarbonyloxy-1,4-phenylene(1-methylethylidene)-1,4-phenylene]
Bisphenol A-phosgene polymer
Bisphenol A polycarbonate
Poly-4,4'-isopropylidenediphenyl carbonate)
2,2-bis(4-Hydroxyphenyl)propane polycarbonate