1) Primary Al_3Fe Compound
初生Al_3Fe化合物
2) primary Al3Pe phase
初生Al_3Fe相
3) Primary Carbide
初生碳化物
1.
Orientation control of primary carbide in Fe-Cr-C hardfacing alloys;
Fe-Cr-C耐磨堆焊合金中初生碳化物生长方向的控制
2.
The results showed that the morphology evolution of primary carbide experienced three stages as following: primary carbide spheroidizing and refining,growing,dissolving at the holding temperature of 1 300 ℃.
研究了半固态过共晶高铬铸铁坯料部分重熔保温过程中初生碳化物的演变规律。
3.
Morphology of primary carbide was studied with four kinds of hardfacing alloys that contain 3.
5 %的四种耐磨堆焊层微观组织及初生碳化物的形态进行了研究 ,分析了碳对微观组织和力学性能的影响。
4) energetic parameter
初晶化合物
1.
In this paper, the relationship between the energetic parameter f(r) of molten salt system and the ratio of primary crystallization compound has been exa mined.
在测定了ＬｉＣｌＭ′Ｃｌ２ＭＦ系列熔盐相图的基础上，讨论了ＬｉＣｌＭ′Ｃｌ２ＭＦ熔盐体系的初晶化合物摩尔比和溶解能参数的关系，并总结了多元相图中一些初晶化合物的形成规律。
5) primary carbide refinement
初生碳化物细化
补充资料：Fe3Al基金属间化合物高温合金
Fe3Al基金属间化合物高温合金
Fe_(3)Al-base intermetallic compound superalloy
Fe3AI JIJ一nshujlon huahewu gaowen heJinFe3AI基金属间化合物高温合金(F e3AI一baseintermetallie eomPound suPeralloy)以Fe3AI相为基体的金属间化合物高温合金。该合金具有优异的高温抗氧化、抗硫化腐蚀性能，合金密度较小，因为不含贵重元素，故价格低廉，很适合于在高温氧化、硫化腐蚀的环境中工作。Fe3AI合金有两个不足之处:室温很脆，伸长率仅3%左右;高温强度不足。通过添加合金元素铬、硼，采取温加工工艺和合理的热处理制度，基本上解决了室温脆性问题，室温拉伸伸长率提高到15%左右。提高强度的途径是进行合金化，添加错、妮、铝等元素进行固溶强化和析出第二相进行时效强化，使合金室温拉伸强度达到l000MPa，600℃拉伸强度达到560MPa。Fe3AI基金属间化合物高温合金可以制造加热元件、炉子紧固件、热交换器、汽车用管材、石油管道和磁性元件等。该合金在真正走向实用之前，应在冶炼工艺和热加工工艺方面进行改进。 (}马培立卜
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条