1) Silica/polymer nanocomposite emulsion
聚合物/二氧化硅复合乳液
3) SiO2-CeO2 mixed oxide
二氧化硅-氧化铈复合氧化物
4) TiO2-SiO2 composite oxide
钛硅复合氧化物
1.
The TiO2 and TiO2-SiO2 composite oxide were prepared by Sol-gel method and characterized by XRD,BET and DRS.
用溶胶-凝胶法制备了TiO2和钛硅复合氧化物,对样品进行了X射线衍射(XRD)、比表面积测试(BET)和紫外-可见漫反射光谱(DRS)分析,并以甲基橙为模拟污染物,考察了其光催化性能。
2.
Preparative methods of sol-gel,hydrolysis precipitation,hydrothermal synthesis for photocatalysts of TiO2-SiO2 composite oxide at home and abroad are introduced in this paper.
介绍了溶胶–凝胶法、水解沉淀法、水热合成法制备钛硅复合氧化物光催化剂的研究进展,评述了3种制备方法的优缺点以及添加硅对TiO2光催化活性的影响:添加硅后增大了催化剂的比表面积,提高了TiO2晶型转变温度,增强了其表面酸度,生成的Ti—O—Si键抑制了TiO2粒径的增大,拓宽了催化剂的禁带宽度,从而提高了光催化剂的催化活性。
5) complex oxides of silicon and phosphorus
硅磷复合氧化物
6) titania-silica composite oxide
硅钛复合氧化物
1.
Bimodal porous titania-silica composite oxide were prepared via sol-gel method with an addition of nonionic surfactant C16EO10 as the structure-directing agent.
采用正硅酸甲酯和钛酸丁酯作为硅和钛的前驱体,在溶胶-凝胶过程中添加非离子表面活性剂C16EO10作为结构导向剂合成双孔结构硅钛复合氧化物材料。
补充资料：复合乳液聚合
分子式：
CAS号：
性质：又称种子(乳液)聚合，两阶段(或多阶段)乳液聚合，核-壳乳液聚合或复合乳液聚合。为了得到颗粒较大的聚合物，在乳液聚合中，可先加入乳液作为种子，这样在聚合过程中，单体可在加入的种子上继续聚合，而不形成新的微粒，因此可以得到颗粒较大的聚合物，这种聚合称为种子聚合。首先，通过常规的(一般为间歇式)乳液聚合或乳液共聚合制备种子胶乳，然后在种子胶乳存在下进行另一种单体或单体混合物的聚合。是新近发展起来的一种乳液聚合方法。主要用来合成各种具有不同组分以及不同形态特征的复合聚合物胶乳。
CAS号：
性质：又称种子(乳液)聚合，两阶段(或多阶段)乳液聚合，核-壳乳液聚合或复合乳液聚合。为了得到颗粒较大的聚合物，在乳液聚合中，可先加入乳液作为种子，这样在聚合过程中，单体可在加入的种子上继续聚合，而不形成新的微粒，因此可以得到颗粒较大的聚合物，这种聚合称为种子聚合。首先，通过常规的(一般为间歇式)乳液聚合或乳液共聚合制备种子胶乳，然后在种子胶乳存在下进行另一种单体或单体混合物的聚合。是新近发展起来的一种乳液聚合方法。主要用来合成各种具有不同组分以及不同形态特征的复合聚合物胶乳。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条