1) ledeburite eutectic carbide
莱氏体碳化物
2) bainite carbide
贝氏体碳化物
1.
The bainite carbide(Bc) nucleates at the interface of γ/α and grows into austenite and ferrite,and finally is surrounded by ferrite.
指出了过渡性是贝氏体相变的主要特征;提出了贝氏体的新定义和贝氏体相变的新机制;贝氏体相变在晶界形核,晶核是单相贝氏体铁素体(BF),不是BF共析分解;在贫碳区形核,是贫碳的γ→α的无扩散相变,不是切变过程,而是以界面替换原子非协同热激活跃迁方式形核长大;钢中贝氏体碳化物(Bc)在γ/α相界面上形核,向BF中长大,最终被铁素体包围,也是以界面原子热激活跃迁方式进行的。
3) carbide-free bainite
无碳化物贝氏体
1.
The results indicated that the ideal micro-structure of high strength ULCB steel is consists of carbide-free bainite,lath martensite and lower bainite,the microstructure strengthing(including fine strengthing) is the main strengthing mechanism,while the content of vanadium is low,the precipitation strengthing of vanadium isn't easy obtained in high strength ULCB steel.
结果表明,高强度超低碳贝氏体钢理想的显微组织是无碳化物贝氏体、板条马氏体和下贝氏体,组织强化(包括细晶强化)是高强度超低碳贝氏体钢主要的强化方式,低水平的钒含量对析出强化没有贡献。
2.
The carbide-free bainite wheel with high performance is newly developing wheel as railway materials.
无碳化物贝氏体钢车轮是近期研究的一种高性能铁道用车轮,它的显微组织组成物较复杂,用常规的黑白金相技术难以显现和分辨组织细节。
4) carbide-free bainite cast steel
无碳化物贝氏体铸钢
5) carbide-free bainite/martensite steel
无碳化物贝氏体/马氏体(CFB/M)复相钢
6) CFB/M microstructure
无碳化物贝氏体/马氏体混和组织
补充资料：莱氏体
分子式：
CAS号：
性质：钢中相形态之一。含碳4.3％(质量)的铁碳二元系合金在1148℃发生共晶转变所形成的短棒状的奥氏体分布在渗碳体的基体上的转变产物。为纪念德国冶金学家A.莱德堡(Ledebur)而命名。它是一种介稳定组织，硬度比较高，性能较脆。在高速钢(如W18Cr4V)及高碳高铬钢(如Cr12、Cr12MoV)的铸态组织中会形成合金碳化物为骨架的鱼骨状莱氏体，经压力加工和热处理后，可提高钢的红硬性和耐磨性，铸铁中若有莱氏组织，也可提高耐磨性。
CAS号：
性质：钢中相形态之一。含碳4.3％(质量)的铁碳二元系合金在1148℃发生共晶转变所形成的短棒状的奥氏体分布在渗碳体的基体上的转变产物。为纪念德国冶金学家A.莱德堡(Ledebur)而命名。它是一种介稳定组织，硬度比较高，性能较脆。在高速钢(如W18Cr4V)及高碳高铬钢(如Cr12、Cr12MoV)的铸态组织中会形成合金碳化物为骨架的鱼骨状莱氏体，经压力加工和热处理后，可提高钢的红硬性和耐磨性，铸铁中若有莱氏组织，也可提高耐磨性。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。