1) Ultrasonic shot peening
超声波喷丸强化
2) ultrasonic shot-peening
超声喷丸
1.
The ultrasonic shot-peening process is simplified as a single shot projected on a sample,and is simulated based on ANASYS/LS-DYNA software.
将超声喷丸过程简化为单个丸粒撞击试件的模型,应用ANASYS/LS-DYNA软件对过程进行有限元仿真。
4) shot peening
喷丸强化
1.
Experimentation of residual stresses of gear strengthened by shot peening;
喷丸强化齿轮残余应力的实验研究
2.
A review of development in shot peening Titanium alloys;
Ti合金喷丸强化研究进展
3.
Effect of shot peening on fatigue performance of nitrided 40Cr and 30CrMo steels;
喷丸强化对渗氮40Cr和30CrMo钢疲劳性能的影响
5) Shot-peening
喷丸强化
1.
The effect of shot-peening strengthened NiCoCrAlY bonding coat on the resistance to isothermal oxidation of the thermal barrier coating was investigated.
研究了 Ni Co Cr Al Y粘结层表面的喷丸强化处理对热障涂层的抗氧化性能的影响 ,利用 MTS测试了经等温氧化不同时间后的热障涂层内部的结合强度 ,并采用 SEM和XRD观察和分析了涂层的界面结合以及相组成。
2.
The shot-peening and the fatigue tests of 40Cr, 20Cr and 30CrMo steels are conducted.
对几种钢材进行了喷丸强化,疲劳试验,测定了残余应力场和表面粗糙度。
3.
Composite Technics of Shot-peening and Brush-plating for Renovating Gears on Helicopter;
分析了直升机主减速器齿轮电刷镀修复后产生裂纹的成因,通过试验提出了喷丸强化改进措施。
6) shot peening strengthening
喷丸强化
1.
The microstructures of shot peening strengthening layer on Titaniun were studied by optical microscopy (OM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM).
利用光学显微分析(OM)、扫描电子显微分析(SEM)及透射电子显微分析(TEM)对喷丸强化工业纯钛表层组织特征进行了研究。
2.
It carries on using the computer simulation technology to the chassis steel structure shot peening strengthening process the movement simulation, through shot peening the stress, the strain field which the pill craft caused carries on the value simulation, the utilization limited unit law to the projectile hit rear spring material surface stress, the strain distribution has carrie.
本课题从车体钢结构亟需提高其使用寿命的实际需求出发,运用计算机仿真技术对车体钢结构进行喷丸强化过程的运动仿真,通过喷丸工艺引起的应力、应变场进行数值模拟,运用有限单元法对弹丸撞击后钢板材料表面应力、应变的分布进行了数值计算和统计分析。
3.
The surface layer of shot peening strengthening was analyzed with OM,SEM and TEM.
研究了喷丸强化对TC4-DT钛合金材料组织的强化效果;采用金相显微镜、扫描电镜和透射电镜分析材料喷丸强化层。
补充资料：喷丸
喷丸
shot peening
PenW0n喷丸(shot peening)用钢铁丸或玻璃丸喷射金属零件表面的表面防护方法。喷丸处理可提高材料的疲劳强度、抗应力腐蚀能力和表面硬度。通过离心力或压缩空气喷射丸粒，使其以很高的速度冲击零件，可在表面产生塑性变形层，缓和机加工和热处理残留的张应力，形成残余压应力。喷丸处理后零件使用温度不能过高，以免残余压应力消失。钢铁件最高使用温度为260~290‘C，铝件为170‘C。 喷丸处理一般控制喷丸强度达到所需的压应力。影响喷丸强度的主要因素有:丸粒直径、丸粒硬度、喷丸速度、喷射角度和丸粒破碎量。常用的丸粒有铸铁丸、铸钢丸和玻璃丸，直径范围0.15一4mm。中等尺寸的丸粒(直径和6一。.75mm)常用于对金属材料进行喷丸处理。 喷丸处理也可用于表面预处理，消除铸件、锻件或热处理后零件表面的型砂及氧化皮，清理焊渣，还能对扭曲的薄壁零件进行校正。 (李宜)