1) CuO microcrystals
CuO微米晶
2) CuO nanocrystallite
CuO纳米晶
1.
Under ambient temperature and ultrasonication,the CuO nanocrystallite is synthesized in one-step by solid-state reaction.
在室温条件和超声波作用下,通过固相化学反应一步合成了CuO纳米晶,用粉末X射线衍射(XRD)及电子衍射法(ED)分析了固相产物的物相,用透射电镜(TEM)观测粒子的大小、形貌、粒径及粒径分布。
3) SnO_2(CuO) nanocrystalline powder
SnO_2(CuO)纳米晶粉料
4) nano(micro)-crystals
纳米(微米)晶
5) microcrystalline/nanocrystalline
微晶/纳米晶
6) submicron crystalline
亚微米晶
1.
Effects of annealing process on microstructure and properties of cold drawn submicron crystalline Cu-5wt%Cr alloy wires;
退火处理对冷拉拔亚微米晶Cu-5wt%Cr合金组织与性能的影响
2.
Through annealing and high temperature treatment,the recovery and recrystallization,the variations of microstructures and properties,and the thermal stability of submicron crystalline Cu-5%Cr wires after cold drawing have been investigated.
通过对冷拉拔的亚微米晶Cu-5%Cr丝材进行退火及高温热处理,研究其回复与再结晶、组织与性能的变化及其热稳定性。
补充资料：多晶莫来石晶须(纤维)
分子式：
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
CAS号：
性质：莫来石相为主晶相的多晶纤维。化学成分为Al2O3 72％～77％，SiO222％～17％，B2O3 3％～5％，P2O51.5％～3.0％。纤维直径2～7μm，纤维长度20～125μm。使用温度1350℃。多采用溶胶-凝胶法制造。主要用作补强填料，也可作为轻质、隔热保温材料使用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。