1) magnesia-zirconia powder
镁锆砂
1.
According to the requirements above, this paper studied the effect of MgO particle size, MgO granularity, magnesia-zirconia powder size and content, .
本论文综述了低碳镁碳耐火材料的发展概况及目前存在的主要问题,根据其所必须具备的强度、抗氧化性、抗侵蚀性、抗热震性等性能要求,在实验室条件下研究了镁砂临界粒度、镁砂颗粒级配、镁锆砂粒度及加入量、环保沥青加入量对低碳镁碳耐火材料结构与性能的影响。
2) Synthetic magnesia zirconia
合成镁锆砂
3) zircon sand
锆砂
1.
Research and practice of the production technologies for small and medium sized cast steel parts with resin coated zircon sand;
锆砂覆膜砂生产中小型铸钢件工艺的研究与实践
2.
Aims To study the technical properties of zircon sand and PEPSET nobake sand, so as to solve the cast problems caused by the quality of sand.
目的 研究锆砂 /PEPSET树脂自硬砂工艺性能 ,用于解决复杂铝铸件由于型砂质量所带来的铸造问题 。
3.
of zircon sand in our country were reported and reviwed.
报告和点评了我国锆砂进出口、生产、消费、价格和应用等方面的情况和问题。
4) Magnesia
[英][mæɡ'ni:ʒə] [美][mæg'niʒə]
镁砂
1.
X-ray fluorescence spectrometric analysis of magnesia powder pressed into disks;
镁砂的粉末直接压片法X荧光光谱分析
2.
Effect of Cr powder addition on reaction and sintering between magnesia and chromite powders
金属Cr粉末对镁砂-铬矿间反应与烧结的影响
3.
This paper is inclined to present the authors' study results of the inexpensive magnesia sands from Dashiqiao area, Liaoning, to be applied as absorbents.
以辽宁省大石桥市廉价镁砂为主原料,制备具有吸附功能的氧化镁吸附剂。
5) magnesium sand
镁砂
1.
Experiment and Study on Preparation of Magnesium Sand with Low Boron and Low Calcium from Bittern by Rehydration;
再水化法制备低硼低钙卤水镁砂的试验与研究
2.
The effects of granularity distributing of alkalescence refractory bone material of magnesium sand,the inverse proportion of bone material and power,alumina power,adhesive,retarder,the content of water and sinter on bulk density,intensity and sinter temperature are investigated.
介绍了感应熔炼电炉成型炉衬的国内外概况和对耐火材料的质量要求,研究了镁砂质碱性炉衬耐火材料的骨料粒度分布、骨料与细粉(基质)、氧化铝微粉、结合剂、缓凝剂、加水量以及烧结剂对耐火材料体积密度、强度及烧结点等性能的影响。
6) magnesite
[英]['mægnəsait] [美]['mægnə,saɪt]
镁砂
1.
The improved method that calcium oxide and magnesium oxide in magnesite are determined by EDTA titrametric method;
EDTA滴定法测定镁砂中氧化钙和氧化镁的改进
2.
Determination of Silicon and Iron in Magnesite by Atomic Emission Spectrometry;
原子发射光谱法测定镁砂中的硅和铁
3.
The results obtained by this method in the analysis of some samples of magnesite wa.
研究了新显色剂二溴对甲基偶氮磺与钙的反应,建立了直接测定镁砂中钙的光度分析方法。
补充资料：镁稀土锆系铸造镁合金
镁稀土锆系铸造镁合金
magnesium-rare earth- zirconium cast magnesium alloy series
me.x一tugaoxi zhuzao me一hejin镁稀土错系铸造镁合金(magnesiumrareearth一zireonium east magnesium alloy series) 以稀土、错为主要合金化元素的铸造镁合金，高温性能良好，亦称耐热铸造镁合金。该系合金由于在20。~300℃时具有高的强度和抗蠕变性能而受到重视。属于该系合金的中国牌号有ZM一3(o.2%一0.7%Zn，2·5%~4·o%RE，0.5%一1.0%Zr，Mg为余量)，ZM一4(2 .0%一3.0%Zn，2.5%一4.0%RE，0.5%一1.0%Zr，Mg为余量)，ZM一6(0.2%一0.7%Zn，2.0%一2·8%Nd，o·4%一1·o%Zr，Mg为余量)等合金。合金中起热强作用的为稀土元素，随稀土含量的增加合金的强度及耐热性显著提高，但塑性则不断下降;加入足够数量的错能使其晶粒度显著细化，提高合金的室温和高温力学性能，并改善铸造性能;该系合金还有少量的锌，其主要作用是降低合金的线收缩和表面缩陷的倾向。 镁稀土错系铸造镁合金的显微组织特征是由固溶体和分布在晶界上的块状化合物组成。合金在固溶处理人工时效状态下，具有良好的室温和高温力学性能其力学性能见表1。表1镁稀土错系铸造镁合金力学性能二六 镁稀土错系铸造镁合金有较小的结晶温度间隔，而且它们的共晶体有很好的流动性，良好的铸造性能，其缩松、热裂的倾向小，充型能力好，可用于铸造形状复杂和要求气密性的铸件。其铸造工艺性能及物理常数见表2。 表2镁稀土错系铸造镁合金铸造 工艺性能及物理常数襄傀·粼罐不纂纂霍嘿肠翼
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条