1) AMS
铝改性硅溶胶
1.
The structures of aluminium modified silica sol(AMS) and boron modified silica sol(BMS) were investigated with IR,()~(29)Si-NMR、()~(11)B-NMR,()~(27)Al-NMR spectra and TEM(transmission electron microscopy) for the first time.
用IR谱2、9Si-NMR1、1B-NMR和27Al-NMR谱及透射电镜对铝改性硅溶胶与硼改性硅溶胶进行了结构形态与特征的分析研究,首次提出了铝改性硅溶胶与硼改性硅溶胶的结构和形态特征。
2.
The preparation and their application in papermaking of aluminium modified silica sol (AMS) and boron modified silica sol (BMS) were first investigated in China.
系统研究了阳离子聚合物／改性硅溶胶微粒体系的特征应用工艺及其电化学性能，发现阳离子淀粉／改性硅溶胶微粒助留体系的抗剪切能力比阳离子淀粉一元助留体系的强，其中阳离子淀粉／硼改性硅溶胶微粒体系抗剪切能力比阳离子淀粉／铝改性硅溶胶微粒体系的强。
2) Al3+ modified silica gel
铝改性硅胶
1.
Al3+ modified silica gel adsorptive materials were prepared by treating ceramic fiber matrix with sequential impregnation of aqueous solution of sodium silicate(Na2SiO3), acidic aluminium salt.
陶瓷纤维纸经水玻璃、酸性铝盐溶液顺次浸渍得到新型铝改性硅胶吸附材料。
3) modified silica sol
改性硅溶胶
1.
The research and application of modified silica sol for superhydrophobic cotton fabrics;
改性硅溶胶在棉织物超拒水整理中的应用研究
2.
A high-performance and noncombustible organic-inorganic composite coating applied on aluminum alloys was prepared by using an as-synthesized,water-borne modified silica sol by organic silanol.
以合成的水性有机硅改性硅溶胶为基料,在铝合金表面制备了一种具有良好理化性能的不燃有机-无机复合涂层。
4) BMS
硼改性硅溶胶
1.
The structures of aluminium modified silica sol(AMS) and boron modified silica sol(BMS) were investigated with IR,()~(29)Si-NMR、()~(11)B-NMR,()~(27)Al-NMR spectra and TEM(transmission electron microscopy) for the first time.
用IR谱2、9Si-NMR1、1B-NMR和27Al-NMR谱及透射电镜对铝改性硅溶胶与硼改性硅溶胶进行了结构形态与特征的分析研究,首次提出了铝改性硅溶胶与硼改性硅溶胶的结构和形态特征。
2.
The preparation and their application in papermaking of aluminium modified silica sol (AMS) and boron modified silica sol (BMS) were first investigated in China.
选用超滤浓缩硼改性硅溶胶，其最佳条件为：室温下、截留分子量为1万的膜、操作压力为3。
5) aluminosilica sol
铝硅酸溶胶
1.
The aggregation behavior of aluminosilica sol under different pH was studied.
本文研究了铝硅酸溶胶在不同ｐＨ值条件下的聚集特性，发现铝硅酸溶胶加无机酸后的聚集过程是一种聚沉或絮凝过程，无法通过用无机酸调节ｐＨ值的方法使得铝硅酸溶胶胶凝成具有足够强度的凝胶，溶胶在ｐＨ＝７０左右时就开始发生聚沉，在ｐＨ＝３５左右时聚沉速度最快，当ｐＨ≤３０时，不仅已聚集的胶粒又重新分散，而且原始胶粒也分散成小胶粒，溶胶稳定，文中对铝硅酸溶胶在不同ｐＨ值条件下的聚集机理进行了探
6) active aluminosiloxane sol
活性硅铝氧烷溶胶
1.
The active aluminosiloxane sol(particle diameter 6～15μm,ash 30%～60%)was prepared by the reaction of the mixture of 2-methylacrylic acid and aminobenzoic acid with sodium silicate and aluminium nitrate.
２－甲基丙烯酸和对氨基苯甲酸按一定摩尔比混合后与硅酸钠、硝酸铝反应，将制得的活性硅铝氧烷溶胶（粒径为６～１５μｍ，灰分为３０％～６０％）填充到ＮＢＲ胶料中，其硫化胶性能与无填充活性硅铝氧烷溶胶者相比，拉伸强度可提高２～６倍，具有明显的增强作用和硫化促进作用。
补充资料：铝-硅系铸造铝合金
分子式：
CAS号：
性质：以硅为主要合金元素的铸造铝合金。硅的添加量范围为5％～25％，并添加镁、铜等元素，形成亚共晶型、共晶型或过共晶型合金。含硅量为5％～13％的亚共晶型或共晶型合金是工业生产中应用最广泛的铸造铝合金。良好的铸造工艺性能和气密性是它们的主要特点。含硅量在13％以上的过共晶型合金具有热膨胀系数小、耐磨性好等特点。
CAS号：
性质：以硅为主要合金元素的铸造铝合金。硅的添加量范围为5％～25％，并添加镁、铜等元素，形成亚共晶型、共晶型或过共晶型合金。含硅量为5％～13％的亚共晶型或共晶型合金是工业生产中应用最广泛的铸造铝合金。良好的铸造工艺性能和气密性是它们的主要特点。含硅量在13％以上的过共晶型合金具有热膨胀系数小、耐磨性好等特点。