1) irreversible photochromism
光致不可逆变色
2) reversible/irreversible thermochromism
可逆/不可逆热致变色
3) Negative photochrmism
逆光致变色
4) reversible thermochromism
可逆热致变色
1.
A series of different mass ratio organic reversible thermochromism materials were prepared by solid phase synthesis method in this paper, choosing some kinds of alcohol and organic acid compounds as the solvent, crystal violet, malachite green and cresol red as chromophoric reagent and boric acid as delomorphic reagent.
本论文分别以结晶紫内酯、孔雀石绿和甲酚红三种物质为发色剂,以硼酸为显色剂,醇类和有机酸类化合物为溶剂,采用固相法合成制备了一系列不同配比的有机可逆热致变色材料。
5) reversible thermochromatic paper
可逆温致变色纸
1.
The manufacture process of reversible thermochromatic paper and its mechanism of color-change were summarized in details in this paper, the extensive application of the paper was also introduced.
阐述了可逆温致变色纸的制备方法及其变色机理,并介绍了可逆温致变色纸的应用。
6) reverse photochromism
逆光致变色性
补充资料：光致变色功能复合材料
分子式：
CAS号：
性质：光激发下能变颜色的复合材制。光致变色现象的产生主要有三个过程，即激发过程、形成色心过程和消除色心的脱色过程。因此光致变色复合材料中的功能组分必须具备上述作用。典型的光致变色复合材料为光致变色玻璃。(1)在硅酸盐玻璃中加入0.1%的Ce2O3和1%的MnO，并在强还原气氛中进行处理即可为光致变色玻璃。其作用机理为紫色光照射下，首先激发Ce3+的离子，它又使Mn2+激活使之变成Mn3+和电子。Mn3+的存在使玻璃变暗，在不照射的情况下激活过程逆转又使玻璃褪色；(2)CdO-B2O3-SiO2体系也有光致变色效应；(3)含卤化银微小晶体的玻璃亦可发生光致变色，其原因为卤化银晶体发生状态的变化而形成色心。该种光致变色玻璃基复合材料已大量应用于制造变色太阳眼镜来保护眼睛不受紫外线伤害。
CAS号：
性质：光激发下能变颜色的复合材制。光致变色现象的产生主要有三个过程，即激发过程、形成色心过程和消除色心的脱色过程。因此光致变色复合材料中的功能组分必须具备上述作用。典型的光致变色复合材料为光致变色玻璃。(1)在硅酸盐玻璃中加入0.1%的Ce2O3和1%的MnO，并在强还原气氛中进行处理即可为光致变色玻璃。其作用机理为紫色光照射下，首先激发Ce3+的离子，它又使Mn2+激活使之变成Mn3+和电子。Mn3+的存在使玻璃变暗，在不照射的情况下激活过程逆转又使玻璃褪色；(2)CdO-B2O3-SiO2体系也有光致变色效应；(3)含卤化银微小晶体的玻璃亦可发生光致变色，其原因为卤化银晶体发生状态的变化而形成色心。该种光致变色玻璃基复合材料已大量应用于制造变色太阳眼镜来保护眼睛不受紫外线伤害。