1) Cf/Al_2O_3-BN ceramic matrix composite
Cf/Al_2O_3-BN陶瓷基复合材料
2) BN-SiO_2-Al_2O_3 system ceramic composites
BN-SiO_2-Al_2O_3系陶瓷复合材料
3) Cf/SiC composite
Cf/SiC陶瓷基复合材料
1.
Using the mixed powder of Cu,Ti and graphite Cf/SiC composite was brazed to Ti alloy under vacuum condition.
研究用Cu粉、Ti粉、石墨粉组成的混合粉末真空钎焊Cf/SiC陶瓷基复合材料和钛合金,采用X射线衍射、扫描电镜和能谱仪对接头组织结构进行分析。
2.
Using the mixed powders of Cu,Ti and graphite,Cf/SiC composite was brazed to Ti-6Al-4V alloy under vacuum condition.
用Cu粉、Ti粉、石墨粉组成的混合粉末连接Cf/SiC陶瓷基复合材料和TC4钛合金,采用X射线衍射、扫描电镜和能谱仪对接头组织结构进行分析。
5) Cf/SiC-BN composite
Cf/SiC-BN复合材料
1.
Nano-SiC powders, carbon fiber, boron acid and urea were used as raw materials to prepare Cf/SiC-BN composites by hot pressing after impregnation.
以纳米SiC粉、碳纤维、硼酸和尿素为原料,通过浸渍,热压烧结的方法制备Cf／SiC-BN复合材料,并考察有界面和无界面条件下Cf／SiC—BN复合材料的力学性能与微观结构。
6) h-BN/Si3N4 ceramic composite
h-BN/Si3N4陶瓷复合材料
1.
The effects of h-BN content on the fracture behavior and toughness of the h-BN/Si3N4 ceramic composites were investigated.
以亚微米级α-Si3N4和h-BN粉末为原料,Y2O3-Al2O3为助烧剂,采用热压烧结制备了h-BN/Si3N4陶瓷复合材料。
补充资料：陶瓷基复合材料
分子式：
CAS号：
性质：ceramic matrix composite 以陶瓷材料为基体，并以陶瓷、碳纤维和难熔金属的纤维、晶须、晶片和颗粒为增强体，通过适当的复合工艺所构成的复合材料。陶瓷基复合材料主要为改善原陶瓷基体材料的本征脆性，避免突发性破坏，提高其工程可靠性。常用的陶瓷基体有氧化物(如氧化锆和氧化铅)、碳化物(如碳化硅)、氮化物(如氮化硅)等。陶瓷基复合材料由于加入增强体后对其韧性有明显改善，如碳纤维增强硅-铝-氧-氮(sialon)陶瓷的断裂韧性由原基体的2.2MPa·ml/2提高到9.5MPa·ml/2，但其抗弯强度仍维持298MPa。由于陶瓷基复合材料发展历史短，在工艺过程中容易发生界面反应使增强体退化，工艺方法不成熟，尚在研究开发阶段。
CAS号：
性质：ceramic matrix composite 以陶瓷材料为基体，并以陶瓷、碳纤维和难熔金属的纤维、晶须、晶片和颗粒为增强体，通过适当的复合工艺所构成的复合材料。陶瓷基复合材料主要为改善原陶瓷基体材料的本征脆性，避免突发性破坏，提高其工程可靠性。常用的陶瓷基体有氧化物(如氧化锆和氧化铅)、碳化物(如碳化硅)、氮化物(如氮化硅)等。陶瓷基复合材料由于加入增强体后对其韧性有明显改善，如碳纤维增强硅-铝-氧-氮(sialon)陶瓷的断裂韧性由原基体的2.2MPa·ml/2提高到9.5MPa·ml/2，但其抗弯强度仍维持298MPa。由于陶瓷基复合材料发展历史短，在工艺过程中容易发生界面反应使增强体退化，工艺方法不成熟，尚在研究开发阶段。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条