2) aqueous tape casting
水基流延
1.
Research on the fabrication of chip PTCR ceramics by aqueous tape casting method;
水基流延制备片式PTCR陶瓷的研究
2.
The alumina green tapes were fabricated successfully,which had smooth surface,homogeneous microstructure,good flexibility and high strength through aqueous tape casting with pure acrylic emulsion as binders.
利用水基流延法,选用纯丙乳液作为粘结剂,成功制备出表面光滑、结构均匀、柔韧性良好、强度较高的Al2O3生带材料,并发现当分散剂聚丙烯酸铵(PAA-NH4)含量为2。
3.
NH4PA, arnmonium poly(acrylic acid), is an available dispersant for aqueous tape casting of hydrophobic AlN powder, proper addition of which can lead to well dispersed hydrophobic AlN s.
NH4PA是一种适合抗水性AlN粉体水基流延用的有效分散剂，在碱性条件下添加该分散剂有利于抗水性AlN粉体在水溶液中的稳定分散。
3) aqueous gel-tape-casting
水基凝胶流延
1.
The super-thin tape was obtained via the aqueous gel-tape-casting.
采用合成锆钛酸铅粉料,制备固相为49%(体积分数,下同)的浆料,以水基凝胶流延成型工艺流延出超薄料带。
4) aqueous tape-casting
水基流延成型
1.
Green ceramic sheets from 20 to 25μm were made by an aqueous tape-casting system,which was BaTiO3 as ceramic powder and water-soluble acrylic binder as binder in the water-based system.
本文以BaTiO3瓷粉为原料,聚丙烯酸酯类水性粘合剂为载体,通过水基流延成型成功制备了20～25μm的电子陶瓷素坯膜;研究了水性粘合剂对浆料的流变性、流延素坯膜的力学性能及微观结构的影响。
2.
Ni electrode-multilayer ceramic capacitor(Ni-MLCC) was prepared by aqueous tape-casting of X7R with acrylic emulsion as binders.
以聚丙烯酸酯乳液为粘合剂,采用水基流延成型制备镍电极多层陶瓷电容器(Ni-MLCC)。
3.
In this paper,the characters and the development history of tape-casting processing are introduced,and a comparison is made between aqueous tape-casting and traditional tape-casting.
概述了流延成型工艺的特点及发展历程,比较了水基流延成型与传统流延成型技术的优缺点。
5) aqueous tape casting
水基流延工艺
1.
On the base of latex dope technology, the study overcomes some defects of traditional aqueous tape casting by selecting latex binder, and gets a smooth-surface and high-strength green tape to laminat.
本研究在传统水基流延成型工艺的基础上，借鉴乳胶漆的制备技术，选用乳胶作粘结剂，克服了传统水基流延工艺的诸多不足，成功制备出性能良好，并在室温下可直接叠层的流延素片，为更好应用于叠层制造成型奠定了基础。
2.
A new technology of aqueous tape casting process has been developed to produce borosilicate glass-ceramic based low temperature co-fired ceramics(LTCC) green tapes for its low cost,safety and no toxicity advantage with water-based latex as binder.
为实现硼硅酸盐玻璃陶瓷基低温共烧陶瓷生带材料的低成本、安全无毒化生产,采用以水性乳胶作为粘结剂的水基流延工艺进行制备;采用数字旋转黏度计分别对分散剂、固相、粘结剂含量对浆料黏度的影响进行了研究,利用扫描电镜对烧结前后生带材料的微观形貌进行了分析。
6) aqueous tape casting
水系流延
1.
The aqueous tape casting process was developed and investigated for the tape casting of 10mol%-Gd2O3-doped CeO2 nano-particles.
本文研究了10%摩尔分数Gd2O3掺杂CeO2(简称10GDC)纳米粉体的水系流延技术。
2.
95Al2O3 substrates were produced via aqueous tape casting in this paper.
本论文采用水系流延技术制备了95氧化铝陶瓷基片,主要对浆料中各种添加剂的作用作了系统研究。
3.
The influence of two different kinds of dispersants on alumina substrate via aqueous tape casting was studied.
研究了2种不同类型的分散剂对水系流延氧化铝基片的影响。