2) PP/POE blends
PP/POE共混物
1.
The formation, morphology and evolution of PP/POE blends in mixer were researched by SEM and PCM.
利用动态流变仪研究了PP/POE共混物的流变性质。
2.
The morphology development,thermal properties and mechanical properties of PP/POE blends were investigated in details by Fourier transformation SEM patterns, Differential Scanning Calorimetry (DSC), stretch test machine and impact test machine.
对不同共混比例的PP/POE共混物进行了力学性能测试,用SEM表征了注塑样条的相形态发展,用DSC研究了共混物的热性能,探讨共混物力学性能与体系的相形态发展以及PP结晶行为的联系。
3.
The effects of rotor speed,shear rate,temperature and the composition of PP/POE blends on the rheological behaviors of PP/POE blend melts were discussed.
随着POE含量的增加,PP/POE共混物熔体的表观黏度和非牛顿指数表现为负偏差行为,粘流活化能则表现出正负偏差行为,说明PP与POE之间存在一定的相容性。
3) PP/PA6 blends
PP/PA6共混体系
1.
The main factors of influencing PP/PA6 blends properties include the formula,compatilizer,operating condition,mixing equipments and so on.
影响PP/PA6共混体系性能的主要因素有配方、相容剂、操作条件、混合设备等,而混合设备中螺杆构型是影响共混体系性能的关键因素。
4) PVC/PP blend
PVC/PP共混体系
1.
And the compatibilizating effect of A-HPAE on PVC/PP blends was introduced.
合成了接枝率分别为86%和20%的两亲性超支化聚(胺-酯)(A-HPAE),并研究了其对PVC/PP共混体系的增容作用。
5) PA 6/PP
PA6/PP共混体系
6) PP/EVAL blends
PP/EVAL共混体系
补充资料：γ铀混溶体系
分子式：
CAS号：
性质：铀在室温和其熔点之间存在α，β，γ三种同素异形变体。α铀为斜方结构，β铀为四方结构，γ铀为简单的体心立方结构。相变温度为：α→β,667.7℃；，β→γ，774.8℃。相变的发生严重地限制了金属铀作为核反应堆燃料的应用。锆、钼、钛、铌和钉等元素都很易溶于γ铀中，形成组成变化很宽的固溶体。这种固溶体可以在室温下保持γ相，使得各向同性的γ相在很宽的温度范围稳定下来，大大改善材料的尺寸稳定性和耐腐蚀性。具有很大的工艺价值。
CAS号：
性质：铀在室温和其熔点之间存在α，β，γ三种同素异形变体。α铀为斜方结构，β铀为四方结构，γ铀为简单的体心立方结构。相变温度为：α→β,667.7℃；，β→γ，774.8℃。相变的发生严重地限制了金属铀作为核反应堆燃料的应用。锆、钼、钛、铌和钉等元素都很易溶于γ铀中，形成组成变化很宽的固溶体。这种固溶体可以在室温下保持γ相，使得各向同性的γ相在很宽的温度范围稳定下来，大大改善材料的尺寸稳定性和耐腐蚀性。具有很大的工艺价值。