1) composite sol-gel route
复合溶胶-凝胶工艺
2) sol-gel process of ceramic matrix composite
陶瓷基复合材料溶胶-凝胶工艺
3) sol-gel process
溶胶-凝胶工艺
1.
M-type barium ferrite(BaFe12O19) nanopowders were synthesized by a sol-gel process.
以化学计量比的硝酸钡、硝酸铁和柠檬酸为原料采用溶胶-凝胶工艺制备M型钡铁氧体纳米粉体,通过XRD、TEM等测试手段表征粉体的结晶特性及微观结构,并研究反应机理以及烧结温度、保温时间对晶粒尺寸的影响,结果表明:粉体的平均晶粒尺寸为40-70 nm,烧结温度显著影响结晶过程、晶粒尺寸及其分布;烧结温度为800℃,保温时间为0。
2.
The nano-porous SiO_(2) films with high laser damage threshold were prepared by using sol-gel process based on base and acid catalysis.
用溶胶-凝胶工艺在碱性、酸性催化条件下制备具有纳米多孔结构的SiO2薄膜。
3.
2)system were prepared by sol-gel process.
用溶胶－凝胶工艺制备了Ｐｂ_（０。
4) sol-gel technique
溶胶-凝胶工艺
1.
TiO_2 porous film supported on stainless steel mesh as metal substrate was prepared by sol-gel technique with polyethylene glycol(PEG) as template.
采用溶胶-凝胶工艺,以聚乙二醇(PEG)为造孔剂,不锈钢丝网为金属基底,制备了TiO2多孔性薄膜。
2.
12)samples were prepared by the sol-gel technique.
采用溶胶-凝胶工艺制备了La0。
3.
Microcrystalline glass of PbTiO_3-SiO_2 was prepared by sol-gel technique using lead acetate trihydrate, tetrabutyl titanate and silicon tetraethoxide as raw materials.
利用醋酸铅、钛酸四丁酯和正硅酸乙酯为主要原料，采用溶胶－凝胶工艺低温合成了ＰｂＴｉＯ_３－ＳｉＯ_２微晶玻璃。
5) sol-gel method
溶胶-凝胶工艺
1.
Homogeneous and transparent gel-glass with Pb, Ti elements and glass-forming elements was prepared at moderate temperature by using sol-gel method.
采用溶胶－凝胶工艺低温合成含有Ｐｂ、Ｔｉ成份和玻璃相组成成份的均匀透明凝胶，并通过热处理在凝胶玻璃中原位生长出纯净的铁电ＰｂＴｉＯ３微晶。
补充资料：陶瓷基复合材料溶胶-凝胶工艺
分子式：
CAS号：
性质：将含有多种组分的溶液，通过物理或化学的方法，使分子或离子成核制成溶胶，在一定条件下，再经凝胶化处理，获得多组分的复合相的凝胶体，经烧结后可获得所需组分的陶瓷基复合材料。采用溶胶凝胶法制备复合材料，通常有两种：一是先制得复合陶瓷粉末，经成型，烧结而获复合陶瓷材料；二是将复合的溶胶相经凝胶化合直接烧结制得整块陶瓷基复合材料。
CAS号：
性质：将含有多种组分的溶液，通过物理或化学的方法，使分子或离子成核制成溶胶，在一定条件下，再经凝胶化处理，获得多组分的复合相的凝胶体，经烧结后可获得所需组分的陶瓷基复合材料。采用溶胶凝胶法制备复合材料，通常有两种：一是先制得复合陶瓷粉末，经成型，烧结而获复合陶瓷材料；二是将复合的溶胶相经凝胶化合直接烧结制得整块陶瓷基复合材料。