1) early down fault
早期正断裂
2) Early fracture
早期断裂
1.
This paper analyses the cause of early fracture of 20MnSi bars in tensile test by the methods of metallographic and scanning electron microscopes.
采用金相和扫描电镜等手段分析了20MnSi钢筋在力学性能检验中出现早期断裂的原因。
2.
The early fracture of base cylinder for motorcycle vibration absorber was analyzed by electron probe microanalyzer(EPMA) and optical microscope.
采用光学显微镜和电子探针分析仪等分析手段,对ZL107铝合金摩托车减震器底筒的早期断裂进行了分析。
3.
When a blade is given to the scissors by abrasive wheel,the extremelly thick chromium-plating layer will carck and desquamate,thus leading to early fracture of surgical scissors in service.
由于镀层过厚,导致刃部砂轮开刃时镀层开裂和脱落,使剪刀在使用的早期断裂。
3) incipient fracture
早期断裂
1.
The result suggests that the cavity beneath cement concrete pavement slabs and the overloading vehicles are the important factors of incipient fractures of cement concrete pavement slabs.
结果表明 ,水泥混凝土路面板下脱空、超载车辆和重载车辆是造成水泥混凝土路面板早期断裂的重要因
4) early stage of failure
提早断裂期
5) Early fragility fault
早期脆性断裂
6) early fatigue fracture
早期疲劳断裂
1.
The results showed that the stress concentration at the machining groove bottom of semicircular part on the workpiece resulted in the early fatigue fracture of the workpiece.
结果表明:零件断裂属于早期疲劳断裂,零件半圆槽R处底部的加工纹路尖锐产生了较大的应力集中是造成零件断裂的主要原因。
补充资料：4-正庚基苯甲酸-4-正庚基苯酯
CAS：79606-06-7
中文名称：4-正庚基苯甲酸-4-正庚基苯酯
英文名称：4-n-Heptylphenyl 4-n-heptylbenzoate
中文名称：4-正庚基苯甲酸-4-正庚基苯酯
英文名称：4-n-Heptylphenyl 4-n-heptylbenzoate
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条