1) hydrolytic polymaleic anhydride
水解马来酸酐
2) HPMA
水解聚马来酸酐
1.
Synthesis and performance of low phosphoric and high efficient water treatment agent HPMA;
新型水处理剂低膦水解聚马来酸酐的合成
2.
Effects of temperature,pH value of aqueous solution and the concentration of HPMA and permeat agent on corrosion inhibition and dispersal properties of HPMA were studied by method of weight loss.
用失重法研究了水解聚马来酸酐 (HPMA)的缓蚀和分散性能 。
3.
The scale inhibition performance of HPMA-EDTMPS compound scale inhibitor was studied.
对水解聚马来酸酐(HPMA)和乙二胺四亚甲叉膦酸钠(EDTMPS)的复配物阻垢性能进行研究。
3) Hydrolyzed polymaleic anhydride
水解聚马来酸酐
1.
Study on the green synthesis of hydrolyzed polymaleic anhydride;
水解聚马来酸酐的绿色合成研究
2.
Study on cleaner production of hydrolyzed polymaleic anhydride;
水处理剂合成工艺的绿色化研究——水解聚马来酸酐的绿色合成技术
3.
The latest synthesis process of hydrolyzed polymaleic anhydride;
水解聚马来酸酐的最新合成工艺研究
4) hydrolyzed polymaleic anhydride (HPMA)
水解聚马来酸酐(HPMA)
1.
The performance of three scale inhibitors including hydrolyzed polymaleic anhydride (HPMA),1-hydroxyethylidene-1,1-diphosphonic acid (HEDP) and 2-acrylamido-2-methylpropane sulfonic acid (AMPS) as well as their compound was studied by static scale inhibition test.
采用静态阻垢法研究了水解聚马来酸酐(HPMA)、1-羟基乙叉二膦酸(HEDP)、2-丙烯酰胺基-2-甲基丙烷磺酸(AMPS)单剂的阻垢性能以及三者复配后的阻垢协同效应,考察了钙离子浓度、溶液pH以及温度等因素对复配物阻垢性能的影响。
5) containing phosphine hydrolyzed polymaleic anhydride
含膦水解聚马来酸酐
1.
Properties of scale-inhibiting of containing phosphine hydrolyzed polymaleic anhydride to CaSO_4
含膦水解聚马来酸酐对硫酸钙的阻垢性能研究
6) maleic acid
马来酸酐
1.
Synthesis mono polyethylene glycol maleate with maleic acid and polyethylene glycol analysis the influencing factors of the reaction,through test,it was found:under condition of existence of self-made catalyst,Fix mol ratio of polyethylene to glycol maleic acid at 2.
由马来酸酐与聚乙二醇单甲醚合成马来酸双聚乙二醇单甲醚酯,对其影响因素进行分析,通过试验确定在自制复合催化剂条件下,当聚乙二醇单甲醚∶马来酸酐摩尔比为2。
2.
The effect of the grafting of maleic acid (MAH) onto chlorinated polypropylene(CPP) on the surface property was studied.
研究了马来酸酐在氯化聚丙烯分子链上的接枝对其表面性质的影响,探讨了马来酸酐接枝氯化聚丙烯与聚丙烯及金属的粘接作用及耐水性。
3.
The technology for synthesizing of polyaspartic acid with maleic acid as raw material was studied in the three steps of ammonification, polymerization and hydrolyzation.
对以马来酸酐为原料合成聚天冬氨酸的工艺路线分为胺化、聚合、水解三个步骤进行了研究,分别考察三步反应的温度、时间和原料配比条件对产物的平均分子量和阻垢性能的影响,研究结果表明胺化反应最适宜的反应条件是原料配比为MA∶NH3=1∶3,反应时间6h,温度为80℃;聚合反应最适宜的反应温度是230℃,时间是3h;水解反应适宜的温度和时间分别是50℃和30min。
补充资料：水解聚马来酸酐
分子式：[C4H4O4]n[C4H2O3]m
分子量：400-800
CAS号：暂无
性质：该品系有机脂肪酸聚合物，一般分子量为400～800的低分子量的聚电解质，易溶于水；化学稳定性及热稳定性高，分解温度在330℃以上，50%的水溶液为淡黄色粘稠液体，密度≥1.2g/cm3，pH值为1-2。在高温（<350℃）和高pH（8.3）下也有良好阻垢效果；阻垢时间可达100h，可与原油脱水、破乳剂混合使用；毒性小，能被微生物降解，且降解物对人畜及水生动物无害。
制备方法：以马来酸酐为原料，甲苯为溶剂，在过氧化苯甲酰存在下引发聚合而得。
用途：适用于循环冷却水、油田注水、原油脱水、低压锅炉的炉内处理，具有良好的抑制水垢生成和剥离老垢作用，对碳酸盐、磷酸盐有良好的阻垢效果，它还可作为纺织系统中纺织品的漂洗剂。
分子量：400-800
CAS号：暂无
性质：该品系有机脂肪酸聚合物，一般分子量为400～800的低分子量的聚电解质，易溶于水；化学稳定性及热稳定性高，分解温度在330℃以上，50%的水溶液为淡黄色粘稠液体，密度≥1.2g/cm3，pH值为1-2。在高温（<350℃）和高pH（8.3）下也有良好阻垢效果；阻垢时间可达100h，可与原油脱水、破乳剂混合使用；毒性小，能被微生物降解，且降解物对人畜及水生动物无害。
制备方法：以马来酸酐为原料，甲苯为溶剂，在过氧化苯甲酰存在下引发聚合而得。
用途：适用于循环冷却水、油田注水、原油脱水、低压锅炉的炉内处理，具有良好的抑制水垢生成和剥离老垢作用，对碳酸盐、磷酸盐有良好的阻垢效果，它还可作为纺织系统中纺织品的漂洗剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条