1) V-5Cr-5Ti alloy
V-5Cr-5Ti合金
1.
Tests of hot compression of cast V-5Cr-5Ti alloy with constant strain rate were conducted on Gleeble 1500 hot simulator.
在Gleeble1500热模拟材料试验机上对铸态V-5Cr-5Ti合金进行恒定应变速率热压缩模拟实验。
2.
The recrystallization of V-5Cr-5Ti alloy annealed at 900~1100 ℃ was investigated.
研究了V-5Cr-5Ti合金在900~1100℃之间的再结晶规律,概括了V-5Cr-5Ti合金的再结晶动力学机制。
2) Fe-5Cr alloy
Fe-5Cr合金
3) Cu-5Cr
Cu-5Cr合金
1.
STRUCTURE AND PROPERTIES OF THE MECHANICALLY ALLOYED Cu-5Cr ALLOY;
机械合金化Cu－5Cr合金的组织性能研究
4) Al-5Ti-1B Alloy
Al-5Ti-1B合金
1.
Al-5Ti-1B alloy was deformed by equal channel angular pressing(ECAP) with the number of pressing passes being 8 at room temperature.
在室温下对Al-5Ti-1B合金进行8道次等径角挤压试验,并运用X射线衍射仪、光学显微镜和扫描电镜等手段研究了变形前后Al-5Ti-1B合金中第二相的变化。
5) Al-5Ti-0.25C alloy
Al-5Ti-0.25C合金
1.
Microstructure evolution of Al-5Ti-0.25C alloy formed by SCR technique;
SCR技术制备Al-5Ti-0.25C合金的组织演化
6) Al-5Ti-0.2C Master Alloy
Al-5Ti-0.2C合金
补充资料：Ti-13V-11Cr-3A1 alloy
分子式：
CAS号：
性质：β钛合金。成分为钒13％，铬11％，铝3％，余量钛。退火后室温机械性能：抗拉强度862MPa，屈服强度827MPa，延伸率10％，弹性模量10.34×104MPa，HRC硬度32～36。采用真空自耗电弧炉熔炼制取。制造紧固件和较大面积的模锻件。