1) biphase electrode material
复相电极材料
1.
The electrochemical properties of stabilized Al-Mn multi-element doped α-Ni(OH)_2 and biphase electrode materials with nanosized α-Ni(OH)_2 were investigated.
本文以改善Ni/MH电池高容量性能为应用背景,通过化学共沉淀法分别制备出稳定的Al-Mn多元取代α-Ni(OH)_2和含纳米α-Ni(OH)_2复相电极材料。
2) composite electrode materials
复合电极材料
1.
The results show that heat treatment can change species of copper oxide,and these species can influence the electrochemical performance of the composite electrode materials.
通过化学沉积法制备了金属铜氧化物/多孔炭复合电极材料,考察了热处理温度及金属铜氧化物负载量对其理化性能的影响。
2.
The recent progress of the composite electrode materials for supercapaitors has been reviewed and introduced in detail due to their better application perspective.
对超级电容器复合电极材料的研究进展进行了综述。
3) composite electrode material
复合电极材料
1.
The electrodeposition process of PbO 2-WC-ZrO 2 composite electrode material on the stainless steel was studied.
研究了不锈钢基体上复合电沉积PbO2-WC-ZrO2复合电极材料的工艺,并通过研究固体微粒的质量浓度及各种工艺参数对PbO2-WC-ZrO2电极材料的电化学性能的影响规律。
4) Battery anode material
电极复合材料
5) composite materials
复相材料
1.
Secondly, the author would like to introduce homogenization method and multi-scale asymptotic analysis methods proposed and developed by Professor CUI Junzhi (member of CAE),the author and many scientists in the world for the crucial problems on the structures and engineering of composite materials.
然后介绍我与崔俊芝院士及国内外其他学者针对复相材料结构与工程中重要问题 ,建立和发展的均匀化方法和多尺度渐近分析方法 ,重点介绍其基本思想、主要结果、存在的问题以及在材料与工程中的应用。
2.
Ba2LaBiO6/ZnO composite materials are prepared by a traditional solid sintering method.
采用固相烧结法制备了Ba2LaBiO6/ZnO复相材料,研究了Ba2LaBiO6/ZnO复相材料的组成和显微组织对材料电性能的影响:实验样品在较宽的温度范围内均显示了良好的NTC特性;烧结体中的相主要由六方结构的ZnO、立方结构的Ba2LaBiO6及含量很少的未知相组成,样品的平均晶粒尺寸随着材料中ZnO含量的增加有减小的趋势。
3.
Mullite / cordierite composite materials, a new kind of kiln refractory, is applied to various kinds of porcelain products extensively.
本研究是以铝型材厂工业污泥为主原料,一次性合成莫来石/堇青石复相材料,再以合成料研制窑具。
6) multiphase material
复相材料
1.
ZrO_2-Al_2TiO_5 multiphase materials with high strength and low expansion were prepared by partially stabilized zirconia (PSZ)powder with different particle sizes coated with nanosized Al_2TiO_5 by co-precipitation method and then sintered at high tem- perature.
以不同粒径的部分稳定ZrO_2(partially stabilized zirconia,PSZ)粉体为原料,采用共沉淀法包覆Al_2TiO_5纳米颗粒层,经高温烧结制备了高强度低膨胀的ZrO_2-Al_2TiO_5复相材料。
补充资料：贵金属电极材料
分子式：
CAS号：
性质：在化学和电化学中用作电极的贵金属材料。纯铂、纯钯、铂钯合金以及二氧化钌等有着优良的化学稳定性，极好的抗腐蚀能力，导电性能好，以及液化活性强等特性。这些材料可靠性高，使用寿命长是各种电极的理想材料。由于铂族金属稀缺昂贵，它们被镀或涂在电极上使用。常用的方法是在钛、锆、钽电极上涂或镀上二氧化钌或二氧化钯或纯铂、纯钯等。它们广泛用作电解电极、燃料电池电极与阴极防腐电极等。
CAS号：
性质：在化学和电化学中用作电极的贵金属材料。纯铂、纯钯、铂钯合金以及二氧化钌等有着优良的化学稳定性，极好的抗腐蚀能力，导电性能好，以及液化活性强等特性。这些材料可靠性高，使用寿命长是各种电极的理想材料。由于铂族金属稀缺昂贵，它们被镀或涂在电极上使用。常用的方法是在钛、锆、钽电极上涂或镀上二氧化钌或二氧化钯或纯铂、纯钯等。它们广泛用作电解电极、燃料电池电极与阴极防腐电极等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条