1) Corrosion Inhibitor
钢筋缓蚀剂
1.
Study on Corrosion Inhibitors for Reinforcing Steel and Electrochemical Chloride Extraction Applied to Reinforced Concrete Structures;
钢筋缓蚀剂和钢筋混凝土结构电化学除氯的研究
2) corrosion of rebar
钢筋锈蚀
1.
Based on the corrosion test of rebar which was wrapped in concrete in salt-water environment,the effect of ratio of water to cement,the content of admixture and RI-IC2 rust inhibitor on the corrosion of rebar was investigated.
结果表明,水灰比是影响钢筋腐蚀的重要因素之一,相同条件下水灰比越大,钢筋锈蚀越严重;掺入粉煤灰和硅粉后,可有效降低钢筋的腐蚀率;R I—IC2型阻锈剂有良好的阻锈效果,相同掺量下,水灰比越大,其阻锈效果越明显。
2.
It is shown in the paper that addition of fine slag particles admixture in cement will significantly inhibit the corrosion of rebars in concrete.
用线性极化法和交流导纳法对微粒矿渣掺合料对混凝土中钢筋锈蚀的影响进行了研究。
3.
AC admittance technique was used in the measurement of the impedance parameters of the corrosion of rebar of the concrete.
采用交流阻抗谱方法研究了在海水侵蚀条件下不同强度等级混凝土试件的钢筋锈蚀情况;通过复导纳图求得了反映钢筋锈蚀特性的全部阻抗参数,并分析了在海水中浸泡的时间对这些参数的影响。
3) reinforcement corrosion
钢筋腐蚀
1.
Research situation and developing tendency of detecting technology of reinforcement corrosion in concrete;
混凝土中钢筋腐蚀监测技术研究现状及发展趋势
2.
Experimental study of chloride ion′s critical content causing reinforcement corrosion in concrete;
混凝土中钢筋腐蚀的氯离子临界浓度试验研究
3.
Chemical mechanism of reinforcement corrosion in reinforced concrete and the precautions;
钢筋混凝土中钢筋腐蚀的化学机理与防腐措施
4) rebar corrosion
钢筋锈蚀
1.
Contrast and verification of the concrete carbonation model and rebar corrosion model
混凝土碳化及钢筋锈蚀预测模型对比验证
2.
However, it is time-consuming to measure the rebar corrosion using traditional methods, and the anodic potential measurement is limited to qualitative analysis.
混凝土中的钢筋锈蚀为电化学腐蚀,可用电位pH图来描述钢筋在不同体系下的稳定性。
3.
According to the process of the concrete cracking induced by the longitudinal rebar corrosion,the bearing capacity degeneration was divided into three stages: pre-cracking,cracking and splitting.
根据压区纵向钢筋锈蚀导致混凝土胀裂的过程,将小偏心受压构件承载力退化分为混凝土未开裂阶段、开裂阶段和保护层剥落3个阶段;通过分析压区混凝土锈胀开裂前的双向应力状态,开裂后的剪、拉应力状态以及保护层剥落后的失效对小偏心受压柱承载力的影响,建立了相应阶段的构件承载力评估模型;给出混凝土锈胀开裂前的模型参数值并进行承载力计算,结果表明:混凝土锈胀开裂前小偏心受压柱的承载力退化可以忽略不计。
5) reinforcement corrosion
钢筋锈蚀
1.
The identification of reinforcement corrosion based on curvature mode shape;
基于曲率模态的桥梁结构钢筋锈蚀损伤识别
2.
Testing of SCC s reinforcement corrosion and penetrability;
自密实钢筋砼钢筋锈蚀和渗透性检测
3.
Influence of the reinforcement corrosion to the shear capacity of the reinforced concrete members;
钢筋锈蚀对钢筋混凝土构件承载力的影响
6) rebar corrosion
钢筋腐蚀
1.
Restraint measures of rebar corrosion in concrete structure;
混凝土结构钢筋腐蚀的抑制措施
2.
Describes the influence of the concrete JR drop on the results of electrochemical measure- ments carried out on reinforcing steel corrosion in concrete and the resulted errors in judgement or evaluation of rebar corrosion.
介绍了在混凝土介质中进行钢筋腐蚀电化学测量时产生的ＩＲ降对测量结果的影响，以及由此可能造成判断上的失误或评估上的错误。
3.
And different studies of different literatures about the temperature effect on the rebar corrosion induced by carbonation are analyzed and contrasted.
通过分析碳化引起的钢筋混凝土构件中钢筋腐蚀的机理及主要影响因素 ,并通过对不同文献中温度对碳化引起的钢筋腐蚀影响的研究进行对比和分析 ,建立了考虑温度对碳化引起的钢筋腐蚀的近似计算公式 ,为预测由碳化引起的钢筋混凝土构件中钢筋的腐蚀提供了依
补充资料：Hnlh-01炼厂缓蚀剂
该缓蚀剂兼具中和和成膜功能，能有效地阻止腐蚀介质对金属的腐蚀，对环烷酸、二氧化碳腐蚀亦有良好的缓蚀
说明：补充资料仅用于学习参考，请勿用于其它任何用途。