The effects of powder temperature, die temperature, lubricant content and compacting pressure on the behavior of warm compaction at lower temperature were studied.
较系统地研究了低温温压工艺,考察了粉末温度、模具温度、润滑剂含量和压制压力对温压 密度的影响。
2.
In this paper the effects of powder temperature, interior lubricant content and die wall lubricant type on the behavior of die wall lubricated warm compaction were studied.
结果表明,粉末温度在100℃时温压效果最好;Fe-1。
5) P/M superalloy
粉末高温合金
1.
Thermodynamic calculation of equilibrium phases for P/M superalloys;
粉末高温合金平衡相析出行为的热力学对比
2.
High temperature deformation and dynamic recrystallization of a new type of P/M superalloy;
某新型粉末高温合金的高温变形与动态再结晶
3.
Pre-forming design of P/M superalloy disc based on equipotential field
基于类等势场的粉末高温合金盘件预成形设计
6) FGH95 superalloy powders
FGH95高温合金粉末
1.
Carbide and its stability in FGH95 superalloy powders during rapid solidification;
对快速凝固FGH95高温合金粉末中的碳化物及其稳定性进行实验研究,分析了粉末颗粒凝固过程中的热学参数和非平衡溶质分配对碳化物形成过程的影响。
补充资料：绝热温升
分子式：
CAS号：
性质：在绝热反应器中进行放热反应时，由于反应热的释出，使床层和反应物的温度上升，从开始反应的温度上升至绝热反应的最高温度称为绝热温升。最大上升温度应有限制，因为由于温度升高会降低平衡转化率，或导致催化剂的失活，或反应速度太快而容易失控。可以采取将催化剂分为多层的办法，使反应物温度上升至某一数值后便进入催化层间进行换热，降低进入下一层的入口温度。
CAS号：
性质：在绝热反应器中进行放热反应时，由于反应热的释出，使床层和反应物的温度上升，从开始反应的温度上升至绝热反应的最高温度称为绝热温升。最大上升温度应有限制，因为由于温度升高会降低平衡转化率，或导致催化剂的失活，或反应速度太快而容易失控。可以采取将催化剂分为多层的办法，使反应物温度上升至某一数值后便进入催化层间进行换热，降低进入下一层的入口温度。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条