1) LOTC method
热交联法
2) thermal crosslinking
热交联
1.
In order to decrease the content of oxygen in SiC fibers,a new method of curing was studied systematically,that is:low-oxidaiton+thermal crosslinking,or LOTC.
本论文以降低SiC纤维中的氧含量为目的，系统地研究了低预氧化+热交联这种新型不熔化方法——热交联法(LOTC法)。
3) thermal curing
热交联
1.
The polycarbosilane fibers cured by thermal curing are sintered step by s tep.
采用热交联工艺改进传统的空气不熔化工艺,在尽可能少引入氧的情况下实现聚碳硅烷纤维的不熔化处理。
2.
The influence of the thermal curing process on the oxygen content of the fibers, the structure and properties of fibers were systematically studied by means of IR, EA (Element Analyse), SEM and XRD.
采用热交联工艺改进传统的空气不熔化工艺,在尽可能少引入氧的情况下实现聚碳硅烷纤维的不熔化处理,降低连续SiC纤维中的氧含量。
5) thermo-crosslinking
热交联
1.
Synthesis of resole resin and its application in thermo-crosslinking CTP plate;
可熔性酚醛树脂的合成及其在热交联CTP版材中的应用
6) thermo-cure crosslinking
热固交联
1.
In this paper,two kinds of adhesive-uncroslinking and thermo-cure crosslinking were synthesized by emulsion copolymerization with acrylate and vinylidene chloride.
本文以丙烯酸酯类和偏二氯乙烯为原料，采用乳液聚合法，合成了非交联型和抗溶剂性的热固交联型两类专用于涤纶膜与多种材料、特别是与高分子量的感光材料之间粘接的乳胶。
补充资料：部分交联热塑性聚氨酯
分子式：
CAS号：
性质：分子结构中含有轻度化学交联的一类热塑性聚氨酯。由过量的NCO(含量小于O.5％质量)与氨基甲酸酯反应形成脲基甲酸酯，形成部分交联，改善了弹性体的耐化学药品性能，综合性能较好，特别是永久变形和压缩变形小。可采用传统熔融的加工技术成型各种耐油耐磨制件。
CAS号：
性质：分子结构中含有轻度化学交联的一类热塑性聚氨酯。由过量的NCO(含量小于O.5％质量)与氨基甲酸酯反应形成脲基甲酸酯，形成部分交联，改善了弹性体的耐化学药品性能，综合性能较好，特别是永久变形和压缩变形小。可采用传统熔融的加工技术成型各种耐油耐磨制件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。