1) Co-low alloys
低钴合金
2) low-Co hydrogen storage alloy
低钴贮氢合金
1.
Effects of annealing treatment on the rare earth-based low-Co hydrogen storage alloy;
退火对稀土系AB_5低钴贮氢合金的影响
2.
Effects of annealing treatment on low-Co hydrogen storage alloy;
退火对低钴贮氢合金的影响
3.
The results show that low-Co hydrogen storage alloys with high discharge capacity and good cycle stability can be obtained by substituting Cu,Cr,Zn and Fe for Co,and the structure of their phase are same.
结果表明,采用适量的铜、铬、锌及铁替代钴所得到的低钴贮氢合金仍具有较高的放电容量和较好的循环稳定性,而且其相结构并未改变。
3) low-cobalt hydrogen storage alloy
低钴储氢合金
4) low-cobalt cemented carbide scrap
低钴废硬质合金
5) Au-Co alloy
金-钴合金
1.
A sulfite Au-Co alloy plating is developed.
研究了亚硫酸盐电镀金-钴合金工艺,并对镀液和镀层的性能进行测试。
6) An-Co alloy
金钴合金
补充资料：钴合金
分子式：
CAS号：
性质：以钴为基加入其他合金化元素形成的合金。常见的有钴基高温合金和稀土钴硬磁合金。钴基高温合金有变形合金如HA-188[Co-22Ni-22Cr-14(Mo-W)-1Fe-0.1C-0.08La]，S816[Co-20Ni-20Cr-8(Mo-W)-4(Ta-Nb)-4Fe-0.4C]；铸造合金有HA-31[Co-10Ni-25Cr-7.5(Mo-W)-2Fe-0.5C]，WI-52[Co-21Cr-11(Mo-W)-2(Ta-Nb)-2Fe-0.45C]，Mar-M322[Co-21.5Cr-9(Mo-W)-4.5(Ta-Nb)-2.2Zr-1.0C)。这类合金在900～1100℃范围内具有较高的强度和良好的抗热疲劳性能，适用于制作喷气发动机、燃气轮机等高负荷的耐热部件。稀土钴硬磁合金有1-5型合金[Sm-Co5]、2-17型合金[Sm2(Co，Cu，Pe，Zr)17]。其中2-17型合金的成分为50％Co+26％Sm+其他，合金的磁能积为224～248kJ/m3。稀土钴硬磁合金适用于要求磁体体积小、磁场强度大的场合，如精密直流电机、家用电器、磁轴承、电子计算机中的打印机和医疗器械等。
CAS号：
性质：以钴为基加入其他合金化元素形成的合金。常见的有钴基高温合金和稀土钴硬磁合金。钴基高温合金有变形合金如HA-188[Co-22Ni-22Cr-14(Mo-W)-1Fe-0.1C-0.08La]，S816[Co-20Ni-20Cr-8(Mo-W)-4(Ta-Nb)-4Fe-0.4C]；铸造合金有HA-31[Co-10Ni-25Cr-7.5(Mo-W)-2Fe-0.5C]，WI-52[Co-21Cr-11(Mo-W)-2(Ta-Nb)-2Fe-0.45C]，Mar-M322[Co-21.5Cr-9(Mo-W)-4.5(Ta-Nb)-2.2Zr-1.0C)。这类合金在900～1100℃范围内具有较高的强度和良好的抗热疲劳性能，适用于制作喷气发动机、燃气轮机等高负荷的耐热部件。稀土钴硬磁合金有1-5型合金[Sm-Co5]、2-17型合金[Sm2(Co，Cu，Pe，Zr)17]。其中2-17型合金的成分为50％Co+26％Sm+其他，合金的磁能积为224～248kJ/m3。稀土钴硬磁合金适用于要求磁体体积小、磁场强度大的场合，如精密直流电机、家用电器、磁轴承、电子计算机中的打印机和医疗器械等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。