2) direct leaching in dumps
直接堆浸
1.
Because of the high degree of oxidation and clay containing quantity,the ore direct leaching in dumps effect of Zijinshan Gold Mine was no good.
紫金山金矿因矿石氧化程度及含泥量高而直接堆浸效果差,自矿山生产以来进行了一系列工艺性选矿试验,包括直接堆浸和制粒堆浸以及破碎+洗矿+重选+炭浸+堆浸等工艺的研究对比,从技术经济的角度分析各工艺的利弊以及发展前景,得出目前应采用的最佳工艺,并为今后矿山生产发展指明方向。
3) Direct leaching
直接浸出
1.
By theoretical analysis and experimental exploration,a complete hydrometallurgical process flow sheet was determined ultimately:direct leaching by nitric acid—impurity removal from leaching solution—precipitation of nickel sulphide—precipitation of magnesium carbonates—alkaline leaching of acid-leach residue and purifying residue—precipitation of calcium molybdate.
本研究通过理论分析与试验探索,最终确定了硝酸直接浸出原矿—浸出液除杂—沉镍—沉镁—碱浸酸浸渣与净化渣—沉钼这一工艺流程,并通过试验研究,确定了具体的工艺参数。
4) direct extraction
直接浸出
1.
Study on enzyme use in rapeseed direct extraction technology;
菜籽酶法直接浸出工艺的研究
2.
Through simulating the process of batch extraction,the optimal conditions of direct extraction of cottonseed kernel with isopropanol were researched.
以异丙醇为浸出溶剂,模拟实际生产的罐组式浸出工艺,通过测定粕残油研究棉仁直接浸出的最佳工艺参数,并将最佳工艺条件下制得的棉籽油的基本指标与正己烷制得的棉籽油的基本指标进行比较。
5) direct soaking
直接浸种
1.
Study the germinating percentage with intermittent and direct soaking of different living rice seeds.
以间歇浸种与直接浸种两种方法,对不同活力的水稻种子进行发芽率的研究。
补充资料：热浸渗铝镀层
分子式：
CAS号：
性质：用热浸镀方法在钢表面形成的镀铝层。钢件浸入700～730℃的熔融铝液中，表面生成铝铁化合物，同时一部分铝原子渗入钢铁基体形成扩散层。为使镀层与基体金属牢固结合，一般在热浸后还要进行一次900～980℃的高温处理，使镀层软熔扩散，形成合金层。镀层具有优良的耐大气腐蚀性、抗高温氧化性和抗高温硫腐蚀性能。在石油、化工、能源、海洋工程等领域广泛应用。
CAS号：
性质：用热浸镀方法在钢表面形成的镀铝层。钢件浸入700～730℃的熔融铝液中，表面生成铝铁化合物，同时一部分铝原子渗入钢铁基体形成扩散层。为使镀层与基体金属牢固结合，一般在热浸后还要进行一次900～980℃的高温处理，使镀层软熔扩散，形成合金层。镀层具有优良的耐大气腐蚀性、抗高温氧化性和抗高温硫腐蚀性能。在石油、化工、能源、海洋工程等领域广泛应用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。