1) phase transformation at low temperature
低温相转化法
2) method of phase transformation at low temperature
低温相转化
1.
Nanosize Fe3O4 magnetic powder was first synthesized by method of phase transformation at low temperature, then coated by oleic acid.
用低温相转化法制备了小粒径的Fe3O4纳米颗粒,用油酸对纳米颗粒进行了表面处理,溶液pH为6。
3) low temperature phase transition
低温转相
4) solid-state reaction at a low temperature
低温固相化学法
1.
The powders of doped ZnO were synthesized by the solid-state reaction at a low temperature and the co-precipitation method respectively.
分别采用低温固相化学法和共沉淀法合成掺杂ZnO粉体,并用这两种粉体在不同温度下烧结制备了ZnO压敏电阻。
5) low temperature conversion
低温转化
1.
United 7kt/a phosphate acid plant and low temperature conversion technology for potassium chloride, with special pipe reactor and drum granulator, sulfurbased compound fertilizer (specification:141414, 151515, 161616, Cl\+-<3% or Cl\+-<1.
7kt/a磷酸装置与氯化钾低温转化相结合 ,经特制的管道反应器 ,转鼓造粒 ,可生产 14 14 14 ,1515 15 ,16 16 16 ,氯根小于 3% (也可小于 1。
6) solid-state method
低温固相法
1.
Nano-sized MgO were prepared by a solid-state method at lower temperature using MgCl2·6H2O and H2C2O4·2H2O as raw materials and soluble starch and PEG1000 as dispersing agents.
以氯化镁和草酸为原料,分别以淀粉和聚乙二醇1000为分散剂,采用低温固相法制备出不同形貌的纳米氧化镁。
补充资料：相转化
分子式：
CAS号：
性质：相转化是指铸膜液的溶剂体系为连续相的一个高分子溶液，转变为高分子是连续相的一个溶胀的三维大分子网络式凝胶的过程。这种凝胶就构成了相转化膜。例如在铸膜液的制膜过程中，由高分子溶液转化成固相的高分子分离膜。聚砜铸膜液是以N,N-二甲基乙酰胺为连续相的高分子溶液，在平板玻璃上刮制成均匀的液膜后，立即浸入水中，二甲基乙酰胺溶入水里，这就使以溶剂为连续相的高分子溶液，转变成以聚砜为连续相的三维大分子网络式凝胶，形成了聚砜分离膜，这一转变过程，称相转化。