1) Glass Fiber Reinforced PET
玻纤增强PET
2) glass fiber reinforced
玻纤增强
1.
Synthesis of melamine polyphosphate in solvent and the flame-retardancy for glass fiber reinforced PA6;
一步法合成三聚氰胺多聚磷酸盐及其阻燃玻纤增强PA6的研究
2.
Preparation of Glass Fiber Reinforced Flame Retardant PBT Composite;
玻纤增强阻燃PBT复合材料的制备
3.
Series of glass fiber reinforced PET with low warpage have been prepared according to the mechanism and different methods of reduction of warpage.
依据降低翘曲的机理 ,选用不同降低翘曲的方法 ,制备了系列低翘曲玻纤增强PET复合材料。
5) fiberglass reinforced PA
玻纤增强PA
1.
Flame retarded fiberglass reinforced PA66 and PA6 were prepared by adding melamine polyphosphate (MPP).
添加质量分数为25%的MPP,能使玻纤增强PA66的氧指数由20。
6) glass fiber reinforced PA66
玻纤增强尼龙66
1.
The effects of red phosphorus flame-retardant masterbatch on the flame-retardant properties of glass fiber reinforced PA66 were investigated.
研究红磷阻燃母粒对玻纤增强尼龙66(PA66)阻燃性能的影响。
2.
In an attempt to overcome the drawbacks of direct application of red phosphorous in glass fiber reinforced PA66,the preparation technology of red phosphorous-based microcapsule fire retardant by in-situ polymerization was studied.
为克服红磷直接应用于玻纤增强尼龙66中的缺点,研究了用原位聚合法制备微胶囊红磷的工艺,测试了样品的吸湿性以及表面包覆性能,并研究了其用于玻纤增强尼龙66的阻燃性能和力学性能。
补充资料：PC/PET blend PC/PET
分子式：
CAS号：
性质： 共混物一般采用机械共混法制备，具有较好的相容性，尤其当PET/PC在60％～70％/40％～30％的共混比例下相容性最好，若PET含量少于上述比例，则共混物具有两相结构。其特点是：有较优良的拉伸强度和加工流动性，在宽广的温度范围内有很高的冲击强度，悬臂梁冲击强度在室温时为960J/m，在-20℃时仍保持为693J/m。有优异的耐化学腐蚀性，司在汽油、机油中工作，并且无应力开裂。刚性好，耐磨，尺寸稳定。耐热性好，加工工艺性良好等。该类共混物适于制造汽车零件，运动器材，草地及园艺工具，各种工业用机械零件。用此类共混物代替超韧尼龙在高温、低温和化学腐蚀性强的环境中使用，能保持良好的尺寸稳定性。
CAS号：
性质： 共混物一般采用机械共混法制备，具有较好的相容性，尤其当PET/PC在60％～70％/40％～30％的共混比例下相容性最好，若PET含量少于上述比例，则共混物具有两相结构。其特点是：有较优良的拉伸强度和加工流动性，在宽广的温度范围内有很高的冲击强度，悬臂梁冲击强度在室温时为960J/m，在-20℃时仍保持为693J/m。有优异的耐化学腐蚀性，司在汽油、机油中工作，并且无应力开裂。刚性好，耐磨，尺寸稳定。耐热性好，加工工艺性良好等。该类共混物适于制造汽车零件，运动器材，草地及园艺工具，各种工业用机械零件。用此类共混物代替超韧尼龙在高温、低温和化学腐蚀性强的环境中使用，能保持良好的尺寸稳定性。