1) Ag-carried nanometer SiO_2
Ag/ SiO_2无机抗菌剂
1.
Ag-carried nanometer SiO_2 and Cu-carried nanometer SiO_2 were prepared by ion adsorption using nanometer SiO_2 as carrier and Ag~+ or Cu~(2+) as antibacterial active element.
研究了纳米SiO_2对Ag~+和Cu~(2+)的吸附行为,得出结论:反应体系的pH 值、Ag~+加入量、纳米SiO_2 的粒径和比表面积是影响纳米SiO_2 对Ag~+吸附的重要因素;制备Ag/ SiO_2无机抗菌剂的最佳工艺参数是pH 值为9~11、Ag~+加入量为3%~5%、反应时间为30~60min、反应温度为20~40℃;对于Cu/SiO_2无机抗菌剂,在pH10 的铜氨溶液中,Cu~(2+)加入量是影响纳米SiO_2对Cu~(2+)吸附的重要因素。
2) silver-zinc inorganic antibacterial agent
Ag-Zn无机抗菌剂
1.
0% silver-zinc inorganic antibacterial agents have been prepared on the surface of stainless steel using plasma spraying method.
采用等离子喷涂方法在0Cr18Ni9Ti不锈钢基体上制作分别含有不同含量Ag-Zn无机抗菌剂的涂层。
3) Ag series inorganic antibacterial agent
Ag系无机抗菌剂
4) silver-type antimicrobial agent
Ag型抗菌剂
1.
It was found that adding a few silver-type antimicrobial agents could make the PLA film had antimicrobial function,when the content of antibacterial agent was 1% or more than 1%,the antimicrobial effect of the film could achieved 100%.
采用溶液共混的方法制得Ag型抗菌剂含量不同的抗菌聚乳酸(PLA)薄膜试样,研究表明,添加少量Ag型抗菌剂即可使薄膜具有抗菌功能,添加1%的抗菌剂薄膜抗菌率达到100%,且薄膜具有抗菌长效性,Ag型抗菌剂在PLA薄膜中不溶出。
5) nano SiO_2-Ag
纳米SiO_2-Ag
6) nano-Ag antimicrobial agents
纳米Ag型抗菌剂
补充资料：抗菌剂
分子式：
CAS号：
性质：又称卫生整理剂。其作用与防霉剂同。常用的有阳离子型及两性型表面活性剂，如烷基二甲基苄基铵盐、烷基三甲基铵盐、烷基吡啶铵盐、多氯苯酚衍生物、聚氨基单脂肪酸、苯基苯酚等。它们先被吸附于菌体上，然后渗入至细胞膜，抑制菌的繁殖，而起杀菌、防臭与防腐的作用。
CAS号：
性质：又称卫生整理剂。其作用与防霉剂同。常用的有阳离子型及两性型表面活性剂，如烷基二甲基苄基铵盐、烷基三甲基铵盐、烷基吡啶铵盐、多氯苯酚衍生物、聚氨基单脂肪酸、苯基苯酚等。它们先被吸附于菌体上，然后渗入至细胞膜，抑制菌的繁殖，而起杀菌、防臭与防腐的作用。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条