1) carbon alloy
碳合金
1.
The metastable mesophase carbon alloys added with different metallicelements, including Ti/Cu、Ti/Ni into the carbonaceous mesophases.
在对国内外碳质中间相科学研究现状进行了深入分析的基础上,对碳合金制备中的工艺参数、制备手段及这两者对碳合金结构、微观形貌、热稳定性进行了研究。
2.
The purpose of this work is to prepare a mesophase carbon alloy with superior tribological performance and to deposit a carbonaceous thin film by using the mesophase as the target material.
本文以中间相碳微球为母体,利用机械合金化法、高温高压合成法等非平衡制备手段,通过添加活性元素 Fe、Ni、Mo 金属元素粉末,制备了亚稳中间相碳合金,并对碳合金的制备、结构和摩擦性能诸多方面进行了研究。
2) C-Mn alloy
锰碳合金
3) Fe C alloy
铁碳合金
1.
The samples of Fe C alloy were made by means of suspension melting.
采用悬浮熔炼液滴下落法制得铁碳合金试样 ,对试样初期凝固坯壳的自由变形和凝固组织进行了观察分析。
4) Silicon-carbon alloys
硅碳合金
5) carbon-manganese alloy
碳锰合金
1.
The carbon and sulphur in carbon-manganese alloy are measured with CS800 infrared C-S measurer and with iron filings and tungsten grain as flux.
以铁屑、钨粒作助熔剂,用CS800红外碳硫仪测定碳锰合金中的碳硫,该法简便、准确可靠、分析结果满意,回收率为98。
6) iron-carbon alloy
铁碳合金
1.
Three kinds of Iron-Carbon alloys are used for studying the effect of the curvature of phase and grain boundaries on the nucleation and growth of super cooled austenitic decomposed structures.
采用了三种工程常用的铁碳合金,观察、分析了晶界、相界曲率对溶质分布的影响及过冷奥氏体分解产物的成核与生长。
补充资料：钼锆铪碳合金
分子式：
CAS号：
性质：由较高含量的锆、铪和碳与钼组成的钼合金。各成分质量百分含量为锆0.4～0.7、铪1.2～2.1、碳0.15～0.27。一种新型钼合金，标记为ZHM钼合金。它们的室温拉伸强度比TZM钼合金约高出40%～50%，是强度最高的钼合金。由粉末冶金烧结成锭后在1200℃锻造加工，变形量50%～75%或更高，中间经8h1200℃的氢气退火。不同的加工及热处理对合金最后的性能影响很大。这种合金尚处于开发阶段，主要由锭加工成盘材，作为粉末高温合金的等温锻造模具。
CAS号：
性质：由较高含量的锆、铪和碳与钼组成的钼合金。各成分质量百分含量为锆0.4～0.7、铪1.2～2.1、碳0.15～0.27。一种新型钼合金，标记为ZHM钼合金。它们的室温拉伸强度比TZM钼合金约高出40%～50%，是强度最高的钼合金。由粉末冶金烧结成锭后在1200℃锻造加工，变形量50%～75%或更高，中间经8h1200℃的氢气退火。不同的加工及热处理对合金最后的性能影响很大。这种合金尚处于开发阶段，主要由锭加工成盘材，作为粉末高温合金的等温锻造模具。