2) S/N characteristics
应力-疲劳特性
4) strain fatigue
应变疲劳
1.
Influence of strain fatigue on J_(IC)-ductile fracture toughness of 20G steel;
应变疲劳对20G钢材延性断裂韧度J_(IC)的影响
2.
Influence of strain fatigue on J_(IC)—the ductile fracture toughness of steels;
应变疲劳对钢材延性断裂韧度J_(IC)的影响
3.
Study on strain fatigue behavior of magnesium alloy AZ91;
AZ91镁合金的应变疲劳行为研究
5) repeated strain
疲劳应变
6) fatigue property
疲劳特性
1.
The results show that test piece's thickness influences the fatigue property of micro-arc oxidation test pieces with differ.
研究表明,试件厚度影响微弧氧化后不同膜厚的试件疲劳特性,试件厚度为2mm时,膜厚10~20μm微弧氧化对试件疲劳寿命有提高;试件厚度3mm时,膜厚10~25μm,微弧氧化使试件疲劳寿命略有降低;预腐蚀疲劳实验表明,微弧氧化试件腐蚀疲劳寿命比普通阳极化试件的腐蚀疲劳寿命高。
2.
The test results show that the fatigue property curve and the cyclic stress-strain curve of LZ50 axletree steel perfectly conform to double logarithm linear relationship.
研究了LZ50车轴钢的循环相关特性,循环疲劳特性及循环应力-应变关系。
3.
Using 810 Material Test System, the fatigue property of ceramic coatings on LY12-CZ aluminum matrix material surface was investigated.
微弧氧化是一种新兴的表面改性技术,利用810MaterialTestSystem疲劳试验机,对LY12-CZ铝合金微弧氧化后疲劳特性进行了研究。
补充资料：ADS疲劳试验
分子式：
CAS号：
性质：考察橡胶裂口增长的一种疲劳试验方法，该法由E. E. Auer、K. W. Doak和I. J. Schaffiner三人首先提出，也由此而得名。试验利用德墨西亚疲劳试验机测定初始割口直径Φ0.93mm在屈挠频率为287次/min下，割口增长和300%定伸应力变化情况。
CAS号：
性质：考察橡胶裂口增长的一种疲劳试验方法，该法由E. E. Auer、K. W. Doak和I. J. Schaffiner三人首先提出，也由此而得名。试验利用德墨西亚疲劳试验机测定初始割口直径Φ0.93mm在屈挠频率为287次/min下，割口增长和300%定伸应力变化情况。