2) Thermoplastic elastomer
热塑弹性体
1.
Progress of modification research of SBS thermoplastic elastomer;
热塑弹性体SBS的改性研究进展
2.
NBR/HDE thermoplastic elastomer was prepared by dynamically vulcanized.
用动态硫化方法制备了NBR／HDPE共混型热塑弹性体，电子显微镜研究其形态表明，尽管NBR的用量超过了HDPE，但NBR仍为分散相，HDPE为连续相，使该材料表现出热塑性。
3) TPE
热塑弹性体
1.
THE COMPATIBILIZED CROSSLINKING TECHNIQUES OF DYNAMICALLY VULCANIZED TPEs;
动态硫化共混型热塑弹性体的增容交联技术
2.
Development of TPE for Li/MnO_2 button cell;
Li/MnO_2扣式电池热塑弹性体的研制
3.
The developments of thermopldstic eldstomers in the world are reviewed in this paper,including TPO,SBC,TPU,TPEE,TPAE etc.
本文综述介绍了国外热塑弹性体的进展，包括聚烯烃、苯乙烯、聚氮酯、聚酯、聚酰胺五大系列热塑弹性体。
4) Thermoplastic elastomers
热塑弹性体
1.
Polarization modification of SBS thermoplastic elastomers and its application;
SBS热塑弹性体的极性化改性及其应用
5) thermoplastic elastomer, TPE
热塑性弹体
6) thermoplastic elastomers
热塑性弹性体
1.
Advancement of fully dynamically vulcanized EPDM/PP thermoplastic elastomers;
EPDM/PP热塑性弹性体研究进展
2.
Attempts were made to prepare thermoplastic elastomers (TPEs) based on linear low density polyethylene (LLDPE) and ground tire rubber (GTR) with dynamic vulcanization.
通过红外光谱、热分析(DSC)和扫描电镜(SEM)对共混物的热行为和表面形态研究表明,加入DCP交联剂使LLDPE、SBS和胶粉之间发生了交联反应,从而增加了胶粉颗粒与LLDPE间的界面相容性,使其热塑性弹性体的力学性能得以提高。
3.
TPE can act as a substitute of rubber in many applications especially in automobile industry in China, which is developing in full speed offering ample potentials for the development of various thermoplastic elastomers.
热塑性弹性体 (TPE)是一类应用广泛兼具有橡胶和塑料特性的高分子材料。
补充资料：SEBS热塑性弹性体
SEBS是饱和型SBS，或称氢化SBS，是由特种线型SBS加氢使双键饱和而制得．结构式见图。SBS在催化剂存在下适度定向加氢．则使聚丁二烯链段氢化成聚乙烯(E)和聚丁烯(B)链段，故称为SEBS。同样，SIS氢化后使其中的聚异戊二烯转变为聚乙烯(E)和聚丙烯链段，则得饱和型SIS(SEPS)。
氢化SBS一般比较坚硬,刚性较强，模量较高，拉伸强度比加氢前有显著提高．扯断伸长率下降。SEBS由于分子链中双键没有或甚少，放对光、氢、臭氧的耐老化性能明显变好。
相对密度 0.90-0.92
拉伸强度 20～30MPa
扯断伸长率 70～160