1) Cu/Mo/Cu cladding sheets
Cu/Mo/Cu复合板
2) Mo/Cu rod
Mo/Cu复合棒
3) Mo-Cu composite powders
Mo-Cu复合粉
1.
Preparation of Nanocrystal Mo-Cu composite powders by Chemical Coprecipitation -Closed Circulation Hydrogen Reduction;
化学共沉淀-封闭循环氢还原法制备纳米Mo-Cu复合粉
4) Mo-Cu composite powder
Mo-Cu复合粉末
1.
Mo-Cu composite powders were prepared by gelatinization-coreduction method,in which gels were obtained from precursors of(NH4)6Mo7O24.
干凝胶经煅烧、还原后,获得Cu含量为20%(质量分数)的Mo-Cu复合粉末。
2.
The Mo-Cu Composite powder was prepared by high energy balling,and the sintering densification behavior and evolution of microstructure and properties of the mechanically alloyed Mo-Cu composite powder in the process of sintering were studied by optical microscope,XRD,SEM and TEM.
采用高能球磨方法制备了超细Mo-Cu复合粉末,通过X射线衍射,金相显微镜,扫描电镜和透射电镜等方法研究分析了所制备Mo-Cu粉末的烧结致密化、显微组织及性能的变化,并与未球磨粉末的烧结试样进行了比较。
5) Mo/Cu
Mo/Cu复合材料
1.
55% , 60% and 67% Mo/Cu composites for electronic packaging applications were fabricated using patent-squeeze casting technology.
5%,Mo的体积分数分别为55%,60%,67%三种Mo/Cu复合材料,并对其进行了组织观察,结果表明:Mo/cu复合材料组织均匀,没有明显的孔洞和缺陷。
6) Cu/Mo composite powder
Cu/Mo复合粉体
1.
By using Sn-Pd catalyst system,the electroless plating Cu on the surface of Mo powder was performed to fabricate Cu/Mo composite powder.
利用Sn-Pd催化体系在Mo粉表面化学镀Cu制备了Cu/Mo复合粉体,利用XRD,SEM,EDS和XPS对复合粉体的成分及形貌进行了分析。