2) waterborne inorganic einc-rich primer
水性无机富锌底漆
3) water borne inorganic zinc-rich coatings
水性无机富锌涂料
1.
are added in ordinary water borne inorganic zinc-rich coatings,Organic filming basal material and corrosion retarding material,so that the construction adaptability of water borne inorganic zinc-rich coatings is greatly expanded,the adhesion of the coating,compactness,anti-ager and anti-slippery performance are remarkablely improved.
在常见的水性无机富锌涂料中,添加有机成膜基料和缓蚀性材料,使水性无机富锌涂料的施工适应性大大拓宽,改善了涂膜的附着性、致密性、耐老化性和抗滑移性。
4) waterborne inorganic zinc silicate coating
水性无机硅酸富锌涂料
5) inorganic zinc-rich
无机富锌
1.
The curing mechanism of inorganic zinc-rich painting is very special and the application must be carried out very carefully especially the thickness of film and the environmental humidity must be in the correct scope.
无机富锌涂料是海洋平台涂装中经常使用的一种底漆,它不但具有优良的防腐蚀性能,同时也能够形成对基体钢材的阴极保护。
6) inorganic zinc rich coating
无机富锌漆
1.
In this article, we have discussed the category, property and application of aqueous inorganic zinc rich coating at home nowadays.
讨论了目前国内水性无机富锌漆的种类、性能和应用 ,比较了几种代表性的水性无机富锌漆及其优点 ,探索了无机富锌漆的性能改进 ,从环保角度出发 ,水性无机富锌漆具有良好的开发前
补充资料：无机富锌车间底漆
分子式：
CAS号：
性质：此类涂料主要由基料、锌粉、着色颜料、填充料和添加剂等组成。基料起黏结锌粉的作用，主要品种有硅酸烷基酯、硅酸烷基酯/钛酸烷基酯、硅酸烷基酯/硼酸烷基酯及其他改性品种。锌粉一般用超细锌粉，颗粒度0.2～12μm，平均粒度5μm，用量50％～80％。施工干膜厚一般20μm左右，兼具电化学保护和化学防蚀双重作用。户外耐久性可达6～8个月，适用于周期较长、防腐蚀要求较高的场合(如造船业防腐)。