1) gas metal arc welding wire
气体保护焊丝
2) twin wire gas shielded arc welding
双丝气体保护焊
1.
7A52 aluminum alloy was welded by using 5A56 filler with twin wire gas shielded arc welding.
采用5A56焊丝对7A52铝合金进行双丝气体保护焊,对焊接接头的力学性能和显微组织进行了研究。
3) flux-cored arc welding
药芯焊丝气体保护焊
1.
Metal droplet transfer characterization in flux-cored arc welding (FCAW) was studied using arc voltage fluctuation value from instantaneous droplet transfer before short-circuiting.
利用焊接过程中熔滴还没有发生短路瞬间的电弧电压变化量ΔU可以区分药芯焊丝气体保护焊(FCAW)熔滴过渡特征,绘制了一定焊接条件下的金属过渡模式图,为最终确定FCAW的最佳工艺参数(焊接电流、电弧电压等)提供指导,可实施长时间在线监控熔滴过渡过程。
4) twin-wire co-pool gas-shielded metal arc welding
双丝共熔池气体保护焊
1.
In order to reveal the mechanism of the twin-wire co-pool gas-shielded metal arc welding(TCGMAW) and to optimize the corresponding welding parameters,the mathematical model describing the fluid flow in the molten pool is investigated.
为了解双丝共熔池气体保护焊的工艺机理,优化工艺参数,对其熔池流场数学模型进行了研究。
5) steel for CO 2 welding
气体保护焊丝用钢
6) welding wire for Ar rich mixed gas shielded welding
富氩混合气体保护焊丝
补充资料：气体保护焊焊丝
气体保护焊焊丝
gas shielded arc welding wire
q{t}baohuhon hans{气体保护焊焊丝(gas shielded are weldingwire)气体保护电弧焊的专用焊丝。根据制造方法的不同，也分为实芯焊丝和药芯焊丝两大类。在中国，目前主要采用实芯焊丝，但药芯焊丝正在迅速推广，并有广阔的应用前途。在日本，实芯焊丝的用量仍大于药芯焊丝，但药芯焊丝的品种更多些，有碳钢用的、低合金高强钢用的、低温钢用的、耐热钢用的和不锈钢用的等各种焊丝，也有适于堆焊用的各种药芯焊丝。根据焊接方法和保护气体的不同，可分为TIG焊丝、MIG焊丝和MAG焊丝。TIG焊丝是配合纯Ar作保护气体，焊丝成分与焊缝成分相接近。MIG焊丝配合Ar+2%O:或Ar+5%CO:保护气体，主要用于焊接沐锈钢等高合金钢。MAG焊丝可配合A:加5%以上的COZ或Ar加2%以上的O:保护气体，也可采用100%CO:作保护气体。后一种保护气体成本低，广泛用于焊接碳钢、低合金钢及不锈钢等，也可用于堆焊。一于一;厂飞之下几澳万随着保护气体中CO:或O:含量的增加，电弧气氛的氧化性增强，要求焊丝中应含有足够量的脱氧剂，如硅、锰等。 (尹士科)