1.
Co-substituted Ni(OH)2 samples were prepared by homogeneous precipitation from nickel nitrate solution in presence of urea,and their structures and electrochemical performance were investigated in order to improve the electrochemical performance of Ni(OH)2 electrodes.
为了提高氢氧化镍电极的电化学性能,以硝酸镍为主盐,采用尿素均相沉淀法制备了钴取代氢氧化镍样品,并对其结构和电化学性能进行了表征与测试。
5) aluminum substituted nickel hydroxide
铝代氢氧化镍
6) nickel hydroxide
氢氧化镍
1.
Preparation and characterization of nano-scale nickel hydroxide using hydrothermal synthesis method;
纳米氢氧化镍的水热合成及其表征
2.
ICP-OES Determination of Main Content and Impurity in Nickel Hydroxide;
氢氧化镍中主含量及杂质含量的ICP-OES测定方法
3.
Research on preparation and electrochemical performances of nano-sized nickel hydroxide;
纳米级氢氧化镍制备及电化学性能研究
补充资料：氧化镍
NiO 分子量74．71
粉末状固体，色泽根据锻烧温度不同而至黑灰色或绿色。密度6.67g／cm3。熔点1990℃。溶于酸和氨水、热过氯酸、热硫酸，不溶于水、浓氨。空气中加热到400℃时，吸收氧变为三氧化二镍，600℃时又还原为氧化镍。经低温假烧制得的氧化镍具有化学活性。经1000℃高温煅烧制得的一氧化镍活性小，而且随制备温度的升高，密度和电阻增加，溶解度和催化活性降低。
应用领域 搪瓷工他用作瓷釉的密着剂和着色剂。陶瓷工业用作色料的原料。磁性材料生产中用作镍锌铁氧体的原料。玻璃工业用作茶色玻璃和显象管玻壳的着色剂。也是制造镍盐及镍催化剂的原料。
粉末状固体，色泽根据锻烧温度不同而至黑灰色或绿色。密度6.67g／cm3。熔点1990℃。溶于酸和氨水、热过氯酸、热硫酸，不溶于水、浓氨。空气中加热到400℃时，吸收氧变为三氧化二镍，600℃时又还原为氧化镍。经低温假烧制得的氧化镍具有化学活性。经1000℃高温煅烧制得的一氧化镍活性小，而且随制备温度的升高，密度和电阻增加，溶解度和催化活性降低。
应用领域 搪瓷工他用作瓷釉的密着剂和着色剂。陶瓷工业用作色料的原料。磁性材料生产中用作镍锌铁氧体的原料。玻璃工业用作茶色玻璃和显象管玻壳的着色剂。也是制造镍盐及镍催化剂的原料。