1) DC arc discharge plasma CVD
直流弧光放电PCVD法
2) DC arc PCVD
直流弧光PCVD
3) DC arc discharge
直流电弧放电法
1.
Intermetallic Ni-Sn nanoparticles were prepared by DC arc discharge method and the thermal stabilityy was investigated.
采用直流电弧放电法制备Ni-Sn纳米粒子,研究了纳米粒子的结构、成份、形貌和热稳定性。
4) arc discharge
直流电弧法
1.
BN-coated Co Nanocapsules,Co-Al composite oxide-coated Co nanocapsules and Ag-coated Ni nano-composite powders were prepared by arc discharge and electroless deposition,respectively,using Co-B amorphous,Co-Al alloy,Ni taken as target.
本文利用直流电弧法和化学镀法以Co-B非晶合金、Co-Al合会、Ni为靶材,分别制备了BN包覆Co纳米胶囊、Co-Al复合氧化物包覆Co纳米胶囊和Ag包覆Ni纳米复合粉体。
5) direct current arc discharge
直流电弧放电
1.
AlN nanowires were deposited on the Mo cathode by direct reaction of metal Al and N2, using the direct current arc discharge equipment.
采用直流电弧放电装置,通过金属铝和氮气直接反应,在钼阴极上沉积出大量的AlN纳米线。
2.
Using the direct current arc discharge plasma method,single-crystal wurtzite AlN nanowires are synthesised by direct nitriding metal Al without catalyst and templet.
在无催化剂和模板条件,利用直流电弧放电等离子方法直接氮化金属铝合成纤锌矿结构的单晶AlN纳米线。
6) D.C.PCVD
直流PCVD
补充资料：弧光放电
| 弧光放电 arc discharge 呈现弧状白光并产生高温的气体放电现象。无论在稀薄气体、金属蒸气或大气中，当电源功率较大，能提供足够大的电流（几安到几十安），使气体击穿，发出强烈光辉，产生高温（几千到上万度），这种气体自持放电的形式就是弧光放电。通常产生弧光放电的方法是使两电极接触后随即分开，因短路发热，使阴极表面温度陡增，产生热电子发射。热电子发射使碰撞电离及阴极的二次电子发射急剧增加，从而使两极间的气体具有良好的导电性。弧光放电的特征是电压不高，电流增大的两极间电压反而下降，有强烈光辉。 还有一种弧光放电叫做冷阴极弧光放电，阴极由低熔点材料（如汞）做成。阴极表面蒸发出的蒸气被电离，在阴极表面附近堆积成空间正电荷层，此电荷层与阴极间极为狭窄区域内形成的强电场引起场致发射，使电流剧增，产生电弧。 弧光放电应用广泛。可用作强光光源，在光谱分析中用作激发元素光谱的光源，在工业上用于冶炼、焊接和高熔点金属的切割，在医学上用作紫外线源（汞弧灯），等等。但是大电流电路开关断开时产生的弧火极其有害，应采取灭弧措施。 |