1) High vinyl content silicone rubber
高乙烯基含量硅橡胶
2) vinyl silicone rubber
乙烯基硅橡胶
1.
Research about construction and function of vinyl silicone rubber/modified MMT nm-composite;
乙烯基硅橡胶/改性蒙脱土纳米复合材料结构性能研究
2.
Blending system of methyl vinyl silicone rubber;
甲基乙烯基硅橡胶并用体系研究
3.
The results of line ablation rate,scanning electron microscope and thermal analysis showed that the type of polyorganosiloxane affected the ablative properties of silicone rubber most;the ablative properties of phenyl silicone rubber was superior to that of vinyl silicone rubber.
线烧蚀率、扫描电镜及热分析结果表明 :聚有机硅氧烷生胶的种类对硅橡胶烧蚀性能的影响最大 ,苯基硅橡胶的烧蚀性能优于乙烯基硅橡胶的烧蚀性能 ,生胶的残炭率是影响硅橡胶的烧蚀性能的主要原因 ;芳纶纤维和羟基硅油的用量对硅橡胶的烧蚀性能影响较大 ;气相法白炭黑的用量对硅橡胶烧蚀性能的影响最小 ,纤维和填料的分散状态对硅橡胶的烧蚀性能也有一定影响。
3) vinylsiloxane rubber
乙烯基硅橡胶
1.
Synthesis of addition liquid vinylsiloxane rubber I. Effect of vinyl silicone oil on mechanical property of silicone rubber;
加成型液体乙烯基硅橡胶的研制——Ⅰ.乙烯基硅油等对物理机械性能的影响
4) vinyl-terminated silicone rubber
端乙烯基硅橡胶
1.
High strength silicone rubber compounds were prepared using vinyl-terminated silicone rubber,fumed silica and hydroxy siloxane by intensive mixing method in Z blade mixer.
采用Ｚ桨捏合机，将端乙烯基硅橡胶、气相法白炭黑及羟基硅氧烷进行混炼，制备了高强度硅橡胶混炼胶。
5) polymethylvinylphenylsiloxane gum
甲基乙烯基苯基硅橡胶
补充资料：高强度高抗撕硅橡胶
分子式：
CAS号：
性质：生胶为无色透明，无机械杂质的高黏滞塑性线型高分子化合物，平均分子量35～70万。乙烯基含量0.07％～0.22％，挥发分(150℃×3h)<3％，硫化胶具有较好的物理机械性能，硬度(邵氏A)40～70，拉伸强度≥8.8MPa，撕裂强度≥34.3kN/m，相对伸长率≥400％。可由甲基乙烯基硅橡胶(生胶)、多乙烯基硅油、气相法白炭黑、硫化助剂以及过氧化双(2,4-二氯苯甲酰)等配合混炼而成。广泛用作动态下使用的橡胶件、宇航及航空用橡胶件和硅橡胶指关节等。
CAS号：
性质：生胶为无色透明，无机械杂质的高黏滞塑性线型高分子化合物，平均分子量35～70万。乙烯基含量0.07％～0.22％，挥发分(150℃×3h)<3％，硫化胶具有较好的物理机械性能，硬度(邵氏A)40～70，拉伸强度≥8.8MPa，撕裂强度≥34.3kN/m，相对伸长率≥400％。可由甲基乙烯基硅橡胶(生胶)、多乙烯基硅油、气相法白炭黑、硫化助剂以及过氧化双(2,4-二氯苯甲酰)等配合混炼而成。广泛用作动态下使用的橡胶件、宇航及航空用橡胶件和硅橡胶指关节等。