1) high-slag cement
高掺量矿渣水泥
1.
It has far-reaching meaning on a strategy of sustainable development for the cement industry to activate the potential hydraulicity and to produce high-slag cement (HSC).
如何使矿渣的潜在水硬性得以激发、生产出高掺量矿渣水泥(HSC),对水泥行业的可持续发展战略有深远的意义。
3) GGBS replacement level
矿渣掺量
1.
Test results show that the freeze thaw durability and strength of GGBS concrete are greatly affected by the strength grade,curing regime and GGBS replacement level.
试验表明，强度等级、养护条件、矿渣掺量等因素对矿渣混凝土的强度、抗冻融耐久性有着显著的影响；矿渣混凝土的抗冻融耐久性明显优于同等级的普通混凝土；矿渣掺量愈大，矿渣混凝土的抗冻融耐久性愈
4) High Performance Slag Cement(HPSC)
高性能矿渣水泥
6) slag cement
矿渣水泥
1.
Thermal treatment of flue gas desulphurization gypsum and its effects on some properties of slag cement;
脱硫石膏的热处理及其对矿渣水泥若干性能的影响
2.
Influence of slag grinding method on the strength of slag cement;
矿渣粉磨方式对矿渣水泥强度的影响
3.
The speciality of compressive strength as mixing slag cement with fly ash;
矿渣水泥中掺用大量粉煤灰的抗压强度特性
补充资料：矿渣水泥
分子式：
CAS号：
性质：由硅酸盐水泥熟料加入适量石膏的同时，加人20％～70％的粒化高炉矿渣共同磨细制成的水硬性胶凝材料。简称为矿渣水泥，代号为P·S。有275，325，425，525，625五个标号以及425R，525R两种早强型水泥。矿渣水泥密度为2.8～3.1g/cm3，需水量较少，保水性和抗冻性差。由于减少了熟料，水化热变低，而抗硫酸盐腐蚀能力提高。不宜用于冬季施工和要求早期强度较高的工程，适于高湿度环境和长期处于水下的工程。在28天后强度有可能继续增长而超过普通硅酸盐水泥。用矿渣水泥的混凝土易泌水而不易振捣密实，不宜用于有较高抗渗要求的混凝土。
CAS号：
性质：由硅酸盐水泥熟料加入适量石膏的同时，加人20％～70％的粒化高炉矿渣共同磨细制成的水硬性胶凝材料。简称为矿渣水泥，代号为P·S。有275，325，425，525，625五个标号以及425R，525R两种早强型水泥。矿渣水泥密度为2.8～3.1g/cm3，需水量较少，保水性和抗冻性差。由于减少了熟料，水化热变低，而抗硫酸盐腐蚀能力提高。不宜用于冬季施工和要求早期强度较高的工程，适于高湿度环境和长期处于水下的工程。在28天后强度有可能继续增长而超过普通硅酸盐水泥。用矿渣水泥的混凝土易泌水而不易振捣密实，不宜用于有较高抗渗要求的混凝土。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。