1) positive-negative forming theory
正负成形理论
1.
At present, the research related to positive-negative forming theory of revolving shell is imperfect in some aspects(such as push sinking mechanism of shell), and is deficiency in some aspects(such as forming mechanism of compound bulging).
目前，有关回转壳体正负成形理论的研究，有些方面(如壳体的推压缩径——负成形的机理)不完善，有些方面(如壳体的复合胀形——正成形的机理)还未涉及，而生产实践却迫切需要理论的深入研究。
2) theory form
理论形成
1.
The theory form and the design method of dwelling district planning structure;
居住区规划结构的理论形成及设计方法
4) metal forming theory
成形理论
1.
The progressive die relates to many key technologies including metal forming theory,sheet steel forming process,d.
级进模涉及冲压成形理论、冲压工艺、模具设计与制造以及模具材料中的许多关键技术。
5) electron-position pair production
正负电子对形成
6) normal form theory
正则形理论
1.
On the basis of the normal form theory,a new algorithm of placing PSS considering second order nonlinearity is presented.
在正则形理论指导下,提出了计及2阶模态非线性相关作用的电力系统稳定器(PSS)配置新方法。
2.
The results are identical to the analytical conclusions based on normal form theory,then it is verified that this algorithm can be correctly and effectively used to detect the dominant inertial modes of power systems.
算例结果表明,该方法能准确检测出系统主导低频振荡模式,其结果与正则形理论分析结果相同,进而验证了此方法的正确性和有效性。
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。