1) pellet containing carbon & aluminium bath smelting reduction method
含碳球团铝浴熔融还原法
2) Aluminium bath smelting reduction
铝浴法熔融还原
3) iron bath smelting reduction process
铁浴熔融还原法
1.
This paper proposes a new pyrometallurgical process for treating zinc oxide ore iron bath smelting reduction process, and describes the experimental investigation of the process after analysis of its principle; the zinc oxide dust thus produced contains 95~98% ZnO, 1 6~2 5% PbO, and the zinc volatilization rate is higher than 93%.
提出了氧化锌矿火法处理的新工艺——铁浴熔融还原法 ,分析了其工艺原理 ,用该工艺试验研究制得的锌氧粉 w Zn O95 %～ 98% ,w Pb O1。
4) bath smelting reduction process
铁浴熔融还原
1.
The pilot test of bath smelting reduction process producing stainless master alloy was carried out in a 15 t complex blowing converter.
在15t复吹转炉中进行了不锈钢母液的铁浴熔融还原工业试验，发现铬的收得率不高，且母液含磷过多。
5) melting reduction process
熔融还原法
1.
According to basic principles of the melting reduction process, a treatment of low-grade zinc oxide ores is investigated.
利用熔融还原法的基本原理 ,对低品位氧化锌矿的处理进行研究 ;分析了铁浴熔融还原法和铝浴熔融还原法的基本理论 ,进行了实验研究 ,并各自考察了温度、时间、碱度的影响。
6) carbothermic electric melting method
碳热还原电熔法
1.
This thesis introduces the main application of boron carbide and the advanced carbothermic electric melting method to manufacture high purity boron carbide crystals.
介绍了B4C的主要应用及采用先进的碳热还原电熔法制备高纯B4C晶体的方法。
补充资料：金属铝还原法
分子式：
CAS号：
性质： 是二氧化钛颜料中TiO2含量的一种测定方法，其原理是先用浓硫酸和硫酸铵将二氧化钛试样溶解，在二氧化碳气氛下用金属铝将四价钛还原为三价钛。还原后的溶液以硫氰酸铵作指示剂，用硫酸铁铵标准滴定溶液进行滴定测定之。该方法详见GB1706-93标准。
CAS号：
性质： 是二氧化钛颜料中TiO2含量的一种测定方法，其原理是先用浓硫酸和硫酸铵将二氧化钛试样溶解，在二氧化碳气氛下用金属铝将四价钛还原为三价钛。还原后的溶液以硫氰酸铵作指示剂，用硫酸铁铵标准滴定溶液进行滴定测定之。该方法详见GB1706-93标准。