1) Cold-test characteristic
冷测特性
2) cooling curve test
冷却特性检测
3) cooling characteristic
冷却特性
1.
By the experimental analysis of the cooling characteristic for the quench oil in the heat treatment process,the improvement method of the existing quench oil cooling characteristic in China Yizhong Group Co.
通过对热处理淬火油冷却特性的试验分析,找出了改善一重集团公司热处理厂现有淬火油冷却特性的方法为按适当比例添加68号标准机油。
2.
Using testing equipment,the cooling characteristics of KHP-C aqueous polymer quenchants are studied.
合理改变KHP-C的浓度和初始温度,可以得到不同的冷却特性,从而实现对不同金属材料的淬火处理。
3.
The cooling characteristic of usual qunching oil were measured by pure silver probe.
用纯银探头对一些常用淬火油冷却特性进行了测试。
4) cooling characteristics
冷却特性
1.
The cooling characteristics of a quenchant SST102 were investigated.
对SST102淬火剂的冷却特性进行了探讨。
2.
Results show that a new WGY aqueous soluble medium has excellent cooling characteristics.
介绍了聚合物淬火介质的一些共性特点，对新研制成功并已用于生产的ＷＧＹ型淬火剂的特点及冷却特性进行了描述，并与国内外同类产品进行了比较。
3.
The results show that proper agitation can improve the cooling characteristics of MH quen-chant and increase the quenching quality of steel pieces.
研究了搅拌速度和搅拌方式对ＭＨ介质冷却特性及钢件淬火质量的影响。
5) cooling property
冷却特性
1.
The effect of two kinds of quenching oil affecting on the plate spring are researched by comparing the cooling property of N32 mechanical oil with Jinyu quick & clean quenching oil, analyzing the structure and properties of the samples of 60Si2Mn and 50CrVA steel using two kind of oil.
通过对N32机油和今禹Y15-II快速光亮淬火油的冷却特性的对比研究,以及对采用两种油进行的60Si2Mn和50CrVA钢样品淬火冷却后的组织性能分析,研究了两种油对板簧热处理质量的影响。
6) cooling character
冷却特性
1.
Performance index and cooling characteristic curve of H100 quench oil made by BP Co.
对某齿轮厂使用的BP公司H100淬火油和德国德润宝722淬火油的性能指标和冷却特性曲线进行了测试,根据淬火产品的使用要求,研制了相应的淬火油HSF-3和HSGKD-2,其相关性能和冷却特性曲线完全达到进口油的水平,其中HSF-3淬火油的齿轮变形规律好,优于H100进口油,而价格仅为进口油的1/3～1/2。
2.
The cooling characters of SST201 under different concentrations, temperatures and repeated use were measured.
试验结果表明,浓度、温度、重复使用次数时其冷却特性均有影响;随浓度增大、温度升高、重复使用次数增多,其冷却能力降低。
3.
The cooling characters of SST101 under different concentration, temperature and repeated use was measured.
本文对淬火剂SST101在其不同的浓度、温度及重复使用次数下冷却曲线进行测定,试验结果表明,浓度、温度、重复使用次数对其冷却特性均有影响,且随其浓度增大、温度升高、重复次数增多,其冷却能力降低。