1) Precursor conversion technique
先驱体转化技术
2) precursor infiltration and pyrolysis
先驱体转化
1.
Preparation and property of 2D C/SiC-ZrB_2 composites via precursor infiltration and pyrolysis
先驱体转化法制备2DC/SiC-ZrB_2复合材料及其性能
2.
Based on the high temperature and short-term oxidation environments,2D Cf/SiC-Si composites were prepared by precursor infiltration and pyrolysis.
针对短时高温抗氧化的具体环境,采用先驱体转化工艺制备2D Cf/SiC-Si复合材料。
3.
Silicon carbide fiber reinforced siliconoxycarbide(Si-O-C) composites were fabricated via precursor infiltration and pyrolysis using polysiloxane.
以聚硅氧烷为先驱体,采用先驱体转化法制备SiCf／Si-O-C复合材料,同时测试所得复合材料的弯曲强度、韧性、剪切强度、密度、热膨胀系数、导热系数、耐烧蚀性能。
3) precursor infiltration pyrolysis
先驱体转化
1.
Three dimensional carbon fiber reinforced silicon oxycarbide composites(3D-Cf/Si-O-C) were fabricated via precursor infiltration pyrolysis using polysiloxane(SR249) as precursor and three dimensional carbon fiber as reinforcements.
以三维碳纤维编织物和硅树脂(SR249)为原料,采用先驱体转化法(PIP)制备了3D-Cf/Si-O-C复合材料,考察了先驱体溶液浸渍方式对其力学性能和微观结构的影响。
4) Preceramic polymer conversion technique
陶瓷前驱体转化技术
补充资料：先驱体法碳化硅纤维增强铝基复合材料
分子式：
CAS号：
性质：一种连续纤维增强金属基复合材料。有不含钛(商品名称Nicalon)和含钛(商品名称Tyranno)两种纺丝碳化硅纤维，与铝复合后一般含纤维40％(体积)左右，单向增强时纵向拉伸强度约为700～1000MPa，模量95～120GPa，密度约2.6g/cm3。主要的制造方法为各种液态渗透工艺。为了促进与铝的浸润，常用的制造方法是在超声波的作用下用连续铸造法先制成复合丝，然后再将复合丝热压成各种制品。也可以直接用压力铸造工艺制成各种零件。由于纺丝碳化硅纤维直径细，柔曲性好，此便于制造形状比较复杂的零件。
CAS号：
性质：一种连续纤维增强金属基复合材料。有不含钛(商品名称Nicalon)和含钛(商品名称Tyranno)两种纺丝碳化硅纤维，与铝复合后一般含纤维40％(体积)左右，单向增强时纵向拉伸强度约为700～1000MPa，模量95～120GPa，密度约2.6g/cm3。主要的制造方法为各种液态渗透工艺。为了促进与铝的浸润，常用的制造方法是在超声波的作用下用连续铸造法先制成复合丝，然后再将复合丝热压成各种制品。也可以直接用压力铸造工艺制成各种零件。由于纺丝碳化硅纤维直径细，柔曲性好，此便于制造形状比较复杂的零件。