1) structural behavior under high temperature and pressure
高温高压晶体结构行为
2) high temperature structure behavior
高温结构行为
1.
By using of high temperature XRD data,the high temperature structure behavior of corundum(α-Al_2O_3) with different crystal morphology was studied by comparative crystal chemistry.
利用高温XRD衍射数据,采用温度比较晶体化学研究方法,研究了不同晶形刚玉(-αAl2O3)的高温结构行为,结果表明:粒状刚玉的晶胞参数(a,c)、Al—O键键长LAl—O受热膨胀作用呈对数增大;晶须状刚玉则呈线性增大;粒状刚玉的晶格热膨胀系数(M)总体趋势呈对数增大,且增大趋势近乎一致,表现出各向同性;而晶须状呈线性增大,其晶胞参数(a)的热膨胀系数比晶胞参数(c)大,表现出各向异性。
3) the crystal structure of high T c superconductor
高温超导体晶体结构
4) High temperature compressive deformation
高温压缩行为
5) high temperature crystallization
高温结晶
1.
The kieserite was prepared by high temperature crystallization from the supersaturated solution of MgSO\-4.
硫酸镁溶液高温结晶生成MgSO4·H2 O ,在硫酸镁溶液中加入硼酸降低硫酸镁的极限饱和度 ,增加结晶推动力 ,使硫酸镁溶液的稳定性降低 ,有利于硫酸镁结晶生成MgSO4·H2 O ,提高MgSO4·H2 O的结晶产率 。
6) High-pressure crystallization
高压结晶
1.
Effect of PET molecular weight on high-pressure crystallization behaviours of PET/PC blends;
PET分子量对PET/PC共混体系高压结晶行为的影响
2.
Compounding ratio effect on high-pressure crystallization behaviours of PET/PC blends was investigated by SEM and WAXD measurements.
利用SEM及W AXD等测试手段研究了配比对PET/PC共混物高压结晶行为的影响。
3.
Adding 10%(mass fraction) PC to PET,we obtained plenty of polymer extended-chain single crystals with C axis thickness exceeding 100 μm during the study on the high-pressure crystallization behaviors of PET/PC blends with a self-made piston-cy.
加入10%(质量分数)聚碳酸酯(PC)于聚对苯二甲酸乙二醇酯(PET)中,在研究PET/PC共混体系高压结晶行为的过程中快速合成了大量生长厚度超过100μm的聚合物伸直链晶体,并采用扫描电子显微镜对其进行了深入研究。
补充资料：高温高压滤失量
分子式：
CAS号：
性质： 在模拟井底的高温(80～232℃)、高压(4140～6555Pa)条件下，在API规定的过滤面积(4580mm2±60mm2)和过滤时间(30min)里，钻井液的滤失量(ml)。
CAS号：
性质： 在模拟井底的高温(80～232℃)、高压(4140～6555Pa)条件下，在API规定的过滤面积(4580mm2±60mm2)和过滤时间(30min)里，钻井液的滤失量(ml)。