1) improved Marshall test method
修正的马歇尔法
2) further modified Marshall test method
进一步修正的马歇尔实验方法
3) re-corrected Marshall stability test
再修正马歇尔试验
1.
That the re-corrected Marshall stability test for mould is better to evaluate the formed strength of the emulsified asphalt mixture.
通过比较和分析 ,得到最佳的乳化沥青混合料成型强度评价方法 :成型再修正马歇尔试验。
4) Marshall method
马歇尔法
1.
Marshall method and strength-index method are utilized to determine the optimum asphalt content of ATB respectively.
分别采用马歇尔法和力学强度指标法对沥青稳定碎石混合料进行沥青用量的确定,分析并比较这两种方法的特点,发现马歇尔法设计结果仅能保证混合料符合体积参数要求,易产生级配粗细与沥青需求相左的矛盾,而力学强度指标法确定的沥青用量则趋于一定的沥青膜厚范围。
5) Marshall method
马歇尔方法
6) large Marshall method
大马歇尔法
1.
Aiming at the bituminous stabilized macadam mixtures with 9 types of gradation and 3 types of asphalt,the comparative test study of bituminous stabilized macadam mixtures is carried out systematicly through large Marshall method,superpave rotate compaction method and GTM method.
针对大粒径沥青稳定碎石基层,结合9种级配、3种沥青的沥青稳定碎石混合料,通过大马歇尔法、superpave旋转压实体积法、GTM法对大粒径沥青稳定碎石混合料材料组成设计方法进行了系统的对比试验研究;建立了3种混合料设计方法之间混合料体积及力学指标的关系;在此基础上给出了重载交通条件下大粒径沥青稳定碎石混合料组成设计方法的建议。
补充资料：卡尔·费歇尔滴定法
分子式：
CAS号：
性质：1935年由卡尔·费歇尔提出，主要用于测定无机物和有机物中的微量水分。又称测水滴定法(aquametry)。按摩尔比碘：二氧化硫:吡啶=1:3:10和无水甲醇配制成的试剂称卡尔·费歇尔试剂(Karl Fischer reagent)。原理是碘(I2)在氧化二氧化硫(SO2)时需要定量的H2O，I2+SO2+2H2O=H2SO4+2HI。试剂中的吡啶能中和反应生成的酸，使反应向右进行。总反应式为C5H5N·I2+C5H5N·SO2+C5H5N+H2O=2C5H5N·HI+C5H5N·SO3。试剂中加入无水甲醇以防止产物C5H5N·SO3与H2O发生副反应，C6H6N·SO3+CH3OH-C5H5N·HSO4CH3。确定终点的方法有目视法和电化学方法。目视法是当滴定至溶液由浅黄变为红棕色时即为终点。电化学方法较目视法灵敏、准确。
CAS号：
性质：1935年由卡尔·费歇尔提出，主要用于测定无机物和有机物中的微量水分。又称测水滴定法(aquametry)。按摩尔比碘：二氧化硫:吡啶=1:3:10和无水甲醇配制成的试剂称卡尔·费歇尔试剂(Karl Fischer reagent)。原理是碘(I2)在氧化二氧化硫(SO2)时需要定量的H2O，I2+SO2+2H2O=H2SO4+2HI。试剂中的吡啶能中和反应生成的酸，使反应向右进行。总反应式为C5H5N·I2+C5H5N·SO2+C5H5N+H2O=2C5H5N·HI+C5H5N·SO3。试剂中加入无水甲醇以防止产物C5H5N·SO3与H2O发生副反应，C6H6N·SO3+CH3OH-C5H5N·HSO4CH3。确定终点的方法有目视法和电化学方法。目视法是当滴定至溶液由浅黄变为红棕色时即为终点。电化学方法较目视法灵敏、准确。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条