说明:双击或选中下面任意单词,将显示该词的音标、读音、翻译等;选中中文或多个词,将显示翻译。
您的位置:首页 -> 词典 -> 成形检测
1)  Forming Inspection
成形检测
2)  formation and testing
化成检测
1.
Aiming at the problem of the low efficiency of traditional equipment, based on basic theory of Li -ion battery formation and testing, a new Li-ion battery formation and testing system which is used in digital signal processor (DSP) is designed.
针对常规设备利用效率低的问题,结合锂离子电池化成检测基本理论,提出以DSP为 核心处理器的锂离子电池化成检测系统。
2.
The constant-current power supply is the necessary part of battery formation and testing system,for the quality of its performance not only directly impacts the technology index of device but also affects whether its work is safe and dependable.
而恒流电源作为电池化成检测系统必不可缺的组成部分,性能优劣直接关系到检测设备的技术指标及能否安全可靠地工作。
3)  testing of pile formation
成桩检测
4)  examination of the excavated hole
成孔检测
5)  inspection result
检测成果
6)  Image Test
成像检测
1.
Enhanced X-ray Real Time Image Test of Impact Damage of Composite Material;
冲击损伤的增强X射线实时成像检测
补充资料:主要射出成形材料成形时应注意事项

■主要射出成形材料成形时应注意事项
品  名 注    意    事    项
PVC
聚氯乙烯
1.  产品种类范围非常广(硬质、软质、聚合物等),成型条件各有不同,从熔融至分
解之温度范围很小,尤须注意加热温度。
2. 附着水分少,但成型周期尽可能减少(50℃~60℃热风干燥)。
3. 成型机方面,与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹,故射出操作后,柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高,特别注意熔融情形。第二级加热温度较高,且尽可能使成形周
期缩短,比较安全。


PA
聚醯胺树脂
1. 成型温度比其它材料高,故采用油加热的成形机较适当。
2. 吸湿性大,必须充分干燥。水分对成型品的品质影响甚大(80℃热风干燥约5~6小时)。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1.  同PE,但成形温度必须较高。熔融温度170℃,超过190℃则流动性大增,则毛边增加,
易产生接缝及凹入情形。


PC
聚碳酸脂
1. 吸湿性比尼龙小,但若有些微之水分存在则成型品产生其它色泽或气泡,故必须密封
干燥同时成形时也须预备干燥(120℃之温度4小时)。
2. 加热温度超过320℃时则产生热分解,成品变色,故特别注意温度调节,又成型时的温度调节也非常重要,须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜(130℃~135℃,1小时程度为准)。