1) initial spontaneous magnetic domains
初始自发磁化磁畴结构
2) magnetic domain structure
磁畴结构
1.
The magnetic domain structure variation was analyzed using water-based magnetic fluid.
5Mo合金阻尼性能的影响,采用水基磁流体观察分析了磁畴结构的变化。
2.
The water-based magnetic fluid was used to analyze the magnetic domain structure variation.
5Ti合金阻尼性能的影响,借助水基磁流体分析了磁畴结构变化,以此解释阻尼性能变化的原因。
3.
The water-based magnetic fluid was used to analyze the variation of magnetic domain structure.
5Ti合金阻尼性能的影响,并借助水基磁流体分析了磁畴结构变化,利用扫描电镜分析了晶界析出物的形态及组成。
3) domain structure
磁畴结构
1.
The observations of domain structure show that the fine and homogeneous stripe domains are obtained at the central area, and they turn to the transverse direction at the edge area.
磁畴结构观察表明，样品中心为均匀的细条畴，靠近边缘，磁畴方向转向横向。
2.
Domain structures of the reactively evaporated Co- CoO films have been observed by Lorentz microscopy.
应用Ｌｏｒｅｎｔｚ显微术观察了反应蒸镀的Ｃｏ－ＣｏＯ膜的磁畴结构。
3.
A kind of modified magnetic fluid-Fe3O4 which is used to observe the domain structure with film was prepared by chemical reaction method.
利用化学反应的方法研制了一种带膜观察磁畴结构的改进型磁流体—Ｆｅ３Ｏ４磁流体，并对其生成条件及影响其磁性的因素进行了分析。
4) initial magnetization
初始磁化
5) domain-wall like structure
类磁畴结构
6) structure initialization
结构初始化
补充资料：自发磁化
分子式：
CAS号：
性质：磁有序物质中，相邻离子未满壳层的电子之间有强烈的交换作用。在低于居里温度或奈耳温度且无外加磁场的情况下，这种作用会使相邻原子或离子的磁矩在一定区域内趋于平行或反平行排列，处于自行磁化的状态，称为自发磁化。自发磁化所产生的单位体积内磁矩的矢量和，叫做自发磁化强度。一般自发磁化随环境温度的升高而逐渐减小，当超过居里温度或奈耳温度即全部消失，物质就变成顺磁性物质。由于配位场各向异性，自发磁化取最低能量的结晶学方向。正如电介质在极化后会改变长度一样，磁性材料在磁化后也发生长度变化，即出现磁致伸缩现象。例如铁酸镍(NiFe2O4)饱和磁化时，沿磁化方向缩短45×10-6。陶瓷硬度高，化学稳定性好，铁氧体陶瓷比金属磁性材料的性能优良。利用自发磁化可用于制造磁带录像机(VTR)和电子计算机等的磁头。
CAS号：
性质：磁有序物质中，相邻离子未满壳层的电子之间有强烈的交换作用。在低于居里温度或奈耳温度且无外加磁场的情况下，这种作用会使相邻原子或离子的磁矩在一定区域内趋于平行或反平行排列，处于自行磁化的状态，称为自发磁化。自发磁化所产生的单位体积内磁矩的矢量和，叫做自发磁化强度。一般自发磁化随环境温度的升高而逐渐减小，当超过居里温度或奈耳温度即全部消失，物质就变成顺磁性物质。由于配位场各向异性，自发磁化取最低能量的结晶学方向。正如电介质在极化后会改变长度一样，磁性材料在磁化后也发生长度变化，即出现磁致伸缩现象。例如铁酸镍(NiFe2O4)饱和磁化时，沿磁化方向缩短45×10-6。陶瓷硬度高，化学稳定性好，铁氧体陶瓷比金属磁性材料的性能优良。利用自发磁化可用于制造磁带录像机(VTR)和电子计算机等的磁头。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条