1) crack mouth
裂缝嘴
1.
The fracture energy,the crack mouth opening displacement and the crack tip opening displacement of the specimens were also measured.
为了研究聚丙烯纤维对水泥稳定碎石断裂韧性的影响,通过聚丙烯纤维水泥稳定碎石和普通水泥稳定碎石的三点弯曲试件断裂试验,测得了试件的断裂能、裂缝嘴张开位移和裂缝尖端张开位移,给出了聚丙烯纤维体积掺量的合理范围——0。
2) crack mouth open displacement
裂缝嘴张开位移
1.
The load-deformation curves and crack mouth open displacements(CMOD) of mortars content 0—18% of SBR(styrene-butadiene rubber) latex were acquired by means of three-point bend test on notched mortar samples.
通过对带有切口的砂浆试样进行三点弯曲试验测试,得到了掺量为0—18%的SBR(styrene-butadiene rubber,简称SBR)乳液改性水泥砂浆荷载-变形曲线及相应裂缝嘴张开位移(CMOD),并通过理论计算得到了不同掺量下改性水泥砂浆的有效裂纹长度(aeff)、临界应力强度因子(KsIC)及裂纹尖端张开位移(CTOD)等断裂特征参数。
3) critical crack mouth opening displacement
临界裂缝嘴张开位移
1.
The results show that G_(fF),critical crack mouth opening displacement(δ_(fmc)) as well as critical crack tip opening displacement(δ_(ftc)) of SFHAC increase linearly with the increas.
结果表明:随着φf的增加,GfF、临界裂缝嘴张开位移(fδmc)、临界裂缝尖端张开位移fδtc均线性增加,钢纤维高强混凝土断裂能增益比、临界裂缝嘴张开位移和临界裂缝尖端张开位移的增益比亦基本呈线性增加。
2.
Through wedge splitting tensile test, the effect of the polypropylene fiber dosage upon the stress intensity factor (KpIC), fracture energy (GpF) and critical crack mouth opening displacement (δpmc) of polypropylene fiber reinforced high-strength concrete (HSC) were studied.
通过楔劈拉伸试验,探讨了聚丙烯纤维掺量对聚丙烯纤维高强混凝土断裂韧度(KpIC)、断裂能(GpF)和临界裂缝嘴张开位移(δpmc)的影响。
4) critical crack tip opening di
临界裂缝嘴尖端张开位移
5) cylinder bed interlock machine
嘴锁缝机
6) closing openings at collar-ends by hand stitching
缝合领嘴