1) B phase
含硼相
1.
Constituents and structure are designed with B phase and Pb as the main elements.
以含硼相和铅为主要组元,进行成分和结构设计,制备出兼有中子和γ射线屏蔽特性及一定力学承载能力的集屏蔽/结构一体化的核屏蔽材料。
3) boron phase
硼相
1.
The results show that,when cooling rate is above 10℃/s,martensite structure will be obtained,and boron phase will be precipitated at grain boundary,but disappear when cooling rate is above 20℃/s.
结果表明,当冷速大于10℃/s时,就能得到完全的马氏体组织,但此时晶界会有"硼相"析出,冷速为20℃/s以上时,"硼相"消失。
2.
The results show that the cause of boron brittleness is the precipitation of boron phases.
试验证明 ,形成“硼脆”的原因是“硼相”。
4) boron constituent
硼相
5) boron content
硼含量
1.
Effect of boron content on properties of CaO-B_2O_3-SiO_2 system glass ceramics
硼含量对钙硼硅系微晶玻璃性能的影响
2.
Analysis of uncertainty in determination of boron content in water-soluble fertilizers by ICP-AES
ICP-AES法测定水溶肥料中硼含量的不确定度分析
3.
Adding different boron contents(0.
01%),1 110℃水韧处理后,随着硼含量的增加,硬度随之升高,在220~278 HBS之间变化;同时冲击韧性下降,最高值αk=178。
6) pig iron containing boron
含硼生铁
1.
Oxidation patter of carbon in pig iron containing boron and Fe-C binary system or Fe-C-Si ternary system at different conditions is studied and discussed respectively.
对以含硼生铁为原料直接冶炼硼钢新工艺的关键问题进行了基础研究,为新工艺提供了理论依据。
补充资料：含硼中子毒物
分子式：
CAS号：
性质：天然硼中，丰度占19.6%的10B是很强的热中子吸收剂。硼是非金属，又硬又脆，不易加工，在辐照下因生成的氦释放出来而引起肿胀。实际应用碳化硼、金属硼化物、含硼合金和硼硅酸盐玻璃等含硼材料。溶于水的硼酸溶液在反应堆发生事故时，可喷入堆芯内实现紧急停堆。也可将硼酸溶液混入作为冷却剂的水内，作为可燃毒物补偿后备反应性。
CAS号：
性质：天然硼中，丰度占19.6%的10B是很强的热中子吸收剂。硼是非金属，又硬又脆，不易加工，在辐照下因生成的氦释放出来而引起肿胀。实际应用碳化硼、金属硼化物、含硼合金和硼硅酸盐玻璃等含硼材料。溶于水的硼酸溶液在反应堆发生事故时，可喷入堆芯内实现紧急停堆。也可将硼酸溶液混入作为冷却剂的水内，作为可燃毒物补偿后备反应性。