1) self-crosslinking polyacrylate emulsion
自交联纯丙乳液
1.
The combination of silicone emulsion and self-crosslinking polyacrylate emulsion was used as a binder for preparing a kind of water-borne ultra thin intumescent fire retardant coating for steel structure.
采用聚有机硅氧烷乳液与自交联纯丙乳液的混合乳液为基料,制备了水性超薄膨胀型钢结构防火涂料,并研究了聚合物基料对其性能的影响。
2) self-crosslinked silicone-acrylate emulsion
自交联硅丙乳液
1.
Polymerization technology of self-crosslinked silicone-acrylate emulsion with high-organosilicone content pre-pared by reactive emulsifier was studied.
研究了以反应性乳化剂制备高硅含量自交联硅丙乳液的聚合工艺,结果表明:以反应性乳化剂代替普通乳化剂,采用后交联技术结合种子乳液法,分步控温,并加入丙二醇作为水解抑制剂,可以显著提高自交联硅丙乳液的聚合稳定性,获得高硅含量的自交联硅丙乳液。
5) self crosslinking em ulsion
自交联乳液
1.
The resultsshow ed thata proper thickness ofthe interm ediate of the core shellself crosslinking em ulsion w as needed in order toobtain the optim um film properties.
研究了乳胶粒组成对含有环氧基、氨基和羧基的多层核壳型室温自交联乳液的涂膜性能。
6) pure acrylic emulsion
纯丙乳液
1.
Reseacrh on synthesis of pure acrylic emulsion for coating;
涂料用纯丙乳液合成的研究
2.
A pure acrylic emulsion with "soft core and hard shell" core-shell structure has been prepared by seed emulsion polymerization in semi-continuous process.
利用半连续法种子乳液聚合工艺制备具有软核硬壳核壳结构的纯丙乳液,并用红外光谱、激光粒度测试仪、高倍显微镜等对乳液的性质与结构进行表征。
补充资料：苯丙乳液
苯丙乳液是由苯乙烯和丙烯酸酯单体经乳液共聚而得。乳白色液体，带蓝光。固体含量40～45％，粘度80～1500mPa·s，单体残留量0.5%，PH值8～9。苯丙乳液附着力好，胶膜透明，耐水、耐油、耐热、耐老化性能良好。
苯丙乳液用作纸品胶粘剂，也可与淀粉、聚乙烯醇、羧甲基纤维素钠等胶粘剂配合使用。贮存于5～30 ℃的库房内，贮存期1年。
苯丙乳液用作纸品胶粘剂，也可与淀粉、聚乙烯醇、羧甲基纤维素钠等胶粘剂配合使用。贮存于5～30 ℃的库房内，贮存期1年。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。