1) stress ratio
应力比r
1.
Analysis of components fatigue crack propagation under different stress ratio r;
应力比r对构件疲劳裂纹扩展的影响分析
3) stress ratio
应力比
1.
Influence of stress ratio on fracture behavior of brittle materials and testification of strain criterion of fracture;
应力比对脆性材料断裂影响及应变断裂准则验证
2.
Influence of stress ratio R on threshold value △K_(th) of fatigue crack propagation for welded joints of 09CuPCrNi steel;
应力比R对09CuPCrNi钢焊接接头疲劳裂纹扩展门槛值△K_(th)的影响
3.
Effect of stress ratio on P-da/dN-Δk curve for 40CrMnSiMoVA steel;
应力比对40CrMnSiMoVA钢P-da/dN-Δk曲线影响研究
4) principal stress ratio
主应力比
1.
Effect of principal stress ratio in plane strain condition on void damage evolution;
平面应变下的主应力比对微孔洞损伤演化行为的影响
2.
The tangent Poisson’s ratio of soil increases when the principal stress ratio increases.
通过基于局部变形测量的三轴试验,分析了泊松比的变化规律:在相同的成样方法和控制密度条件下,同一种材料的颗粒排列组合结构基本类似,在不同围压条件下的试样变形规律基本保持一致;随主应力比的增加,切线泊松比也随之增加,建立泊松比与主应力比之间的关系更符合泊松比取值规律。
5) reduced-stress
对比应力
6) axle ratio of stress
应力轴比
补充资料：应力比
分子式：
CAS号：
性质：疲劳试验中，最小和最大应力之比值。拉伸应力取正值，压缩应力取负值。材料发生疲劳断裂区分为两大类型，一种是加载应力水平低，断裂前承载周次多，这种断裂称高周疲劳或应力疲劳；另一种是加载应力水平高，断裂前承载周次少，这种断裂称低周疲劳或应变疲劳。所以，应力比是试验设计者所关心的参数。
CAS号：
性质：疲劳试验中，最小和最大应力之比值。拉伸应力取正值，压缩应力取负值。材料发生疲劳断裂区分为两大类型，一种是加载应力水平低，断裂前承载周次多，这种断裂称高周疲劳或应力疲劳；另一种是加载应力水平高，断裂前承载周次少，这种断裂称低周疲劳或应变疲劳。所以，应力比是试验设计者所关心的参数。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。