1) tamping coke
捣固焦
1.
Research about tamping coke middle platform temperature system;
关于捣固焦加热制度中平台炉温制度的研究
2) stamp-charging coke oven
捣固焦炉
1.
According to the actual application of stamp-charging coke oven in production, based on the basic principle, the technical process characteristic, the engineering design, the trial production situation , its actual existent questions have been analyzed and researched.
根据捣固炼焦在生产中的的应用,从基本原理、工艺流程特点、工程设计、试产情况对南(昌)钢捣固焦炉实际存在的问题进行了分析研究,并针对问题摸索出了一些行之有效的解决问题的方法。
2.
The procedures of heating-up and starting-up a stamp-charging coke oven which burns solid fuel at low temperature are described.
介绍低温环境下捣固焦炉采用固体燃料烘炉和开工所采取的一系列特殊措施。
3) stamping coking
捣固炼焦
1.
According to the requirements for the size and moisture of coal for stamping coking,the size and moisture of coal,the briquette height and the stamping technology are studied,and some appropriate improvement measures are put forward.
根据捣固炼焦原料煤粒度、水分的要求,对煤料粒度、水分、煤饼高度及捣打技术进行了研究,提出了改进措施,提高了煤饼成型率及单孔焦炭产量。
4) Stamp charged coking
捣固炼焦
1.
The clean-type stamp charged coking technology with heat recovery designed in China with independent intellectual property right is internationally unique in the oven structure and the hydraulic stamping facility,which enjoys the advantages of clean production,environmental protection,enlarged carbonization chamber,etc.
其中,我国自主开发设计、具有自主知识产权的QRD清洁型热回收捣固炼焦技术,首次采用独特的炉体结构和液压捣固技术,具有清洁生产、保护环境、炭化室大型化等特点,取得了较好的环境和经济、社会效益。
5) stamping coke oven
捣固焦炉
1.
There were the problems of escaping large amount of crude gas from the oven door and fume substandard discharge during coal charging with wet coal-charging fume elimination and dust removal vehicle for stamping coke oven in a coking plant.
某焦化厂捣固焦炉车载式湿式装煤消烟除尘车没有很好地解决装煤时机侧炉门逸出大量荒煤气和烟气排放不达标问题。
6) tamping coking
捣固炼焦
1.
In order to enlarge utilization coal gas resource,tamping coking process is adopted at Nangang.
介绍了南(昌)钢公司为扩大利用焦煤资源,采用捣固炼焦工艺。
2.
The technological process of coking technology with dry coal in tamping coking,the selection of main equipments and the operation result are described,and the obtained benefit is analyzed.
阐述了捣固炼焦中装入干燥煤炼焦技术的工艺流程、主要设备选型和运行效果,分析了所取得的效益。
3.
In comparison with the top coal loading technique,the tamping coking technique could improve the coke quality and reduce the quality of coal for coking.
捣固炼焦工艺虽然相对于顶装煤工艺可以改善焦炭质量,并能降低炼焦用煤的质量。
补充资料：捣固焦炉
捣固焦炉
stamp-charging coke oven
由。gU jiaolu捣固焦炉(s tam卜charging cok。~n)用捣固法装煤(见煤捣固工艺)炼焦的侧装焦炉。1882年由德国首创，迄今已有100多年的历史。捣固炼焦工艺成熟，易于操作，尤其适合于以高挥发分弱粘结性煤为主的配煤炼焦，因此在一些高挥发分弱粘结性煤储量较多的国家和地区(如法国、德国萨尔地区、波兰、捷克和斯洛伐克以及罗马尼亚等)，捣固焦炉发展较快。中国高挥发分弱粘结性煤也很多，尤其在华东和东北地区，这类煤的储量和产量较多，所以捣固焦炉也得到了一定的发展。早在1919年3月，在鞍山就投产了两座考伯斯式捣固焦炉。1956年，中国自行设计的炭化室高3.Zm的捣固焦炉投产。1970年.又建造了炭化室高3.sm的捣固焦炉。到1990年底，共投产了10座捣固焦炉(共315孔炭化室)，年生产焦炭能力达142万t。从80年代起，由于捣固机械的改进，捣固焦炉也得以大型化。联邦德国萨尔矿业公司(SaarbergGmbH)于1984年在迪林根中央炼焦厂投产了炭化室高6m的大型捣固焦炉，该焦炉一次装煤量为48t，其生产效率可与顶装煤大容积焦炉相当。捣固焦炉的炉体结构与一般顶装煤焦炉没有原则上的差别，但为了适应捣固煤饼侧装，捣固焦炉炉体结构具有以下特点:(1)由于捣固煤饼沿炭化室长向没有锥度，捣固焦炉的炭化室锥度都比较小(0一20~)。(2)为保持煤饼的稳定性，煤饼的高宽比要受到限制。过去认为捣固煤饼的高宽比不能超过9:1，所以捣固焦炉炭化室的高度不能超过4m。80年代以来，随着捣固技术的发展，捣固煤饼的高宽比已增加到巧:1，因而捣固焦炉炭化室高度已达到6m。(3)捣固焦炉的煤饼沿高向和长向的堆密度分布都较均匀(顶装煤焦炉煤料堆密度相差较大)，因此捣固焦炉的加热要与此相适应。(4) 捣固焦炉炭化室底以上第一层炉墙砖，因经常受送煤 饼的托煤板的摩擦冲击，磨损特别严重，故这层砖应 特别加厚。(5)捣固焦炉炉顶不设装煤孔，只须设2一 3个烧除沉积碳和供消烟车除尘用的孔。 (俞震亚秦家骥)